레이저 클래딩 공정을 이용한 Ni-Cr-B-Si + WC/12Co 복합 코팅층의 제조 및 기계적 특성
Manufacturing of Ni-Cr-B-Si + WC/12Co Composite Coating Layer Using Laser Cladding Process and its Mechanical Properties
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this study we manufacture a Ni-Cr-B-Si +WC/12Co composite coating layer on a Cu base material using a laser cladding (LC) process, and investigate the microstructural and mechanical properties of the LC coating and Ni electroplating layers (reference material). The initial powder used for the LC coating layer is a powder feedstock with an average particle size of 125 μm. To identify the microstructural and mechanical properties, OM, SEM, XRD, room and high temperature hardness, and wear tests are implemented. Microstructural observation of the initial powder and LC coating layer confirm the layer is composed mainly of γ-Ni phases and WC and Cr23C6 carbides. The measured hardness of the LC coating and Ni electroplating layers are 653 and 154 Hv, respectively. The hardness measurement from room up to high temperatures of 700°C result in a hardness decrease as the temperature increases, but the hardness of the LC coating layer is higher for all temperature conditions. Room temperature wear results show that the wear loss of the LC coating layer is 1/12 of the wear level of the Ni electroplating layer. The measured bond strength is also greater in the LC coating than the Ni electroplating.
Abstract
In this study we manufacture a Ni-Cr-B-Si +WC/12Co composite coating layer on a Cu base material using a laser cladding (LC) process, and investigate the microstructural and mechanical properties of the LC coating and Ni electroplating layers (reference material). The initial powder used for the LC coating layer is a powder feedstock with an average particle size of 125 μm. To identify the microstructural and mechanical properties, OM, SEM, XRD, room and high temperature hardness, and wear tests are implemented. Microstructural observation of the initial powder and LC coating layer confirm the layer is composed mainly of γ-Ni phases and WC and Cr23C6 carbides. The measured hardness of the LC coating and Ni electroplating layers are 653 and 154 Hv, respectively. The hardness measurement from room up to high temperatures of 700°C result in a hardness decrease as the temperature increases, but the hardness of the LC coating layer is higher for all temperature conditions. Room temperature wear results show that the wear loss of the LC coating layer is 1/12 of the wear level of the Ni electroplating layer. The measured bond strength is also greater in the LC coating than the Ni electroplating.
참고문헌 (23)
- J. D. Majumdar, , Sadhana-Acad. P. Eng. S., 28, pp.495~ (2003)
- X. Wu, , J. Mater. Process. Technol., 135, pp.266~ (2003)
- K. P. Cooper, "Laser surface processing, ASM Handbook", pp.861~ (1992)
- J. M. Yellup, , Surf. Coat. Technol., 71, pp.121~ (1998)
- L. Shepeleva, , Surf. Coat. Technol., 125, pp.45~ (2000)
- A. Riveiro, , Surf. Coat. Technol., 253, pp.214~ (2014)
- O. F. Ochonogor, , Applied Surf. Sci., 263, pp.591~ (2012)
- Q. Ming, , Surf. Coat. Technol., 106, pp.174~ (1998)
- X. Wu, , Surf. Coat. Technol., 141, pp.141~ (2001)
- X. Wang, , Trans. Nonferrous Met. Soc. China, 23, pp.1689~ (2013)
- 박은광, "레이저 클래딩법을 이용한 AISI 316L 스테인리스강 내 Y2O3입자의 분산거동", 한국분말야금학회지, 20(4), pp.269~274 (2013), 한국분말야금학회
- J. Rodriguez, , Wear, 255, pp.950~ (2003)
- E. Fernandez, , Wear, 259, pp.870~ (2005)
- J. M. Miguel, , Tribol. Int., 36, pp.181~ (2003)
- C. T. Kwok, , Surf. Coat. Technol., 107, pp.31~ (1998)
- R. L. Sun, , Surf. Coat. Technol., 132, pp.251~ (2000)
- G. Y. Liang, , Surf. Coat. Technol., 89, pp.121~ (1997)
- R. Gonzalez, , Wear, 262, pp.301~ (2007)
- B. Chao-lei, , Trans. Nonferrous Met. Soc. China, 22, pp.1989~ (2012)
- J. Przybyøowicz, , J. Mater. Process. Technol., 109, pp.154~ (2001)
- J. He, , Surf. Coat. Technol., 157, pp.72~ (2002)
- T. Y. Cho, , Surf. Coat. Technol., 202, pp.5556~ (2008)
- Y. Tang, , Mater. Des., 29, pp.257~ (2008)