탄탈륨 카바이드 분말 특성제어를 위한 원료 전처리 기술
Pre-treatments of initial materials for controlling synthesized TaC characteristics in the SHS process
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
We report the feasibility of TaC production via self-propagating high temperature synthesis, and the influence of the initial green compact density on the final composite particle size. Experiments are carried out from a minimum pressure of 0.3 MPa, the pressure at which the initial green body becomes self-standing, up to 3 MPa, the point at which no further combustion occurs. The green density of the pellets varies from 29.99% to 42.97%, as compared with the theoretical density. The increase in green density decreases the powder size of TaC, and the smallest particle size is observed with 1.5 MPa, at 10.36 μm. Phase analysis results confirm the presence of the TaC phase only. In the range of 0.3-0.5 MPa, traces of unreacted Ta and C residues are detected. However, results also show the presence of only C residue in the matrix within the pressure range of 0.6-3.0 MPa.
Abstract
We report the feasibility of TaC production via self-propagating high temperature synthesis, and the influence of the initial green compact density on the final composite particle size. Experiments are carried out from a minimum pressure of 0.3 MPa, the pressure at which the initial green body becomes self-standing, up to 3 MPa, the point at which no further combustion occurs. The green density of the pellets varies from 29.99% to 42.97%, as compared with the theoretical density. The increase in green density decreases the powder size of TaC, and the smallest particle size is observed with 1.5 MPa, at 10.36 μm. Phase analysis results confirm the presence of the TaC phase only. In the range of 0.3-0.5 MPa, traces of unreacted Ta and C residues are detected. However, results also show the presence of only C residue in the matrix within the pressure range of 0.6-3.0 MPa.
참고문헌 (15)
- W.Y. Jang, , J. Korean Soc. Heat Treat., 13, pp.281~ (2000)
- M.Y. Yang, , J. of the KSME., 30, pp.36~ (1990)
- 홍현선, "The Coating of Cobalt Over Tungsten Carbide Powder by Wet Chemical Reduction Method", 한국분말재료학회지, 21(2), pp.93~96 (2014), 한국분말재료학회
- 이훈석, "타이타늄 하이드라이드 분말의 침탄에 의한 타이타늄 카바이드 분말 제조", 한국분말재료학회지, 24(1), pp.29~33 (2017), 한국분말재료학회[DOI]
- A. Badzian, , Int. J. Refract. Met. Hard Mater., 15, pp.3~ (1997)[DOI]
- A. Nieto, , Scr. Mater., 69, pp.678~ (2013)[DOI]
- Z.Zak Fang, , Int. J. Refract. Met. Hard Mater., 27, pp.288~ (2009)[DOI]
- Y.J. Chen, , Mater. Lett., 56, pp.279~ (2002)[DOI]
- T. Ya. Kosolapova, "Carbides: Properties, Production and Applications" (1971), Plenum Press
- H. Xiang, , Scr. Mater., 55, pp.339~ (2006)[DOI]
- N.A. Hassine, , Int. J. Refract. Met. Hard Mater., 13, pp.353~ (1995)[DOI]
- Pedro Miguel Amaral, , Int. J. Refract. Met. Hard Mater., 18, pp.47~ (2000)[DOI]
- S.A. Shvab, , Powder Metall Met C+, 13, pp.368~ (1974)
- C.L. Yeh, , J. Alloys Compd., 415, pp.66~ (2006)[DOI]
- Arvind Varma, , Adv. Chem. Eng., 24 (1998)