염 보조 초음파 분무 열분해 공정으로 합성된 TiO2 나노입자의 특성에 열분해 온도가 미치는 영향
Effect of Pyrolysis temperature on TiO2 Nanoparticles Synthesized by a Salt-assisted Ultrasonic Spray Pyrolysis Process
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this study, ultrasonic spray pyrolysis combined with salt-assisted decomposition, a process that adds sodium nitrate (NaNO3) into a titanium precursor solution, is used to synthesize nanosized titanium dioxide (TiO2) particles. The added NaNO3 prevents the agglomeration of the primary nanoparticles in the pyrolysis process. The nanoparticles are obtained after a washing process, removing NaNO3 and NaF from the secondary particles, which consist of the salts and TiO2 nanoparticles. The effects of pyrolysis temperature on the size, crystallographic characteristics, and bandgap energy of the synthesized nanoparticles are systematically investigated. The synthesized TiO2 nanoparticles have a size of approximately 2–10 nm a bandgap energy of 3.1–3.25 eV, depending on the synthetic temperature. These differences in properties affect the photocatalytic activities of the synthesized TiO2 nanoparticles.
Abstract
In this study, ultrasonic spray pyrolysis combined with salt-assisted decomposition, a process that adds sodium nitrate (NaNO3) into a titanium precursor solution, is used to synthesize nanosized titanium dioxide (TiO2) particles. The added NaNO3 prevents the agglomeration of the primary nanoparticles in the pyrolysis process. The nanoparticles are obtained after a washing process, removing NaNO3 and NaF from the secondary particles, which consist of the salts and TiO2 nanoparticles. The effects of pyrolysis temperature on the size, crystallographic characteristics, and bandgap energy of the synthesized nanoparticles are systematically investigated. The synthesized TiO2 nanoparticles have a size of approximately 2–10 nm a bandgap energy of 3.1–3.25 eV, depending on the synthetic temperature. These differences in properties affect the photocatalytic activities of the synthesized TiO2 nanoparticles.
참고문헌 (15)
- J. Schneider, , Chem. Rev, 114, pp.9919~ (2014)
- X. Chen, , Chem. Rev, 114, pp.9281~ (2014)
- K. Nakata, , Photochemistry Rev, 13, pp.169~ (2012)
- S. Dong, , Rsc Adv, 5, pp.14610~ (2015)
- Y. -I. Lee, , J. Nanosci. Nanotechnol, 14, pp.8005~ (2014)
- W. Li, , J. Am. Chem. Soc, 135, pp.18300~ (2013)
- R. Thapa, , J. Mol. Catal. A: Chem., 363-364, pp.223~ (2012)
- Q. Qu, , Langmuir, 26, pp.9539~ (2010)
- Z. Cheng, , Ceram. Int, 43, pp.3431~ (2017)
- G. L. Messing, , J. Am. Ceram. Soc, 76, pp.2707~ (1993)
- W. N. Wang, , Ind. Eng. Chem. Res, 47, pp.1650~ (2008)
- 지명준, "염 보조 초음파 분무 열분해법을 이용한 TiO2 나노입자의 합성 및 광학적 성질", 한국분말재료학회지, 26(1), pp.34~39 (2019), 한국분말재료학회[DOI]
- D. Lin, , Chem. Mater, 21, pp.3479~ (2009)
- H. Lin, , Appl. Catal. B, 68, pp.1~ (2006)
- S. G. Kumar, , J. Phys. Chem. A, 115, pp.13211~ (2011)