초음파 분무 열분해와 화학적 변환 공정을 이용한 (GaN)1-x(ZnO)x 나노입자의 합성과 광학적 성질
Synthesis and Optical Property of (GaN)1-x(ZnO)x Nanoparticles Using an Ultrasonic Spray Pyrolysis Process and Subsequent Chemical Transformation
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, (GaN)1-x(ZnO)x solid solution nanoparticles with a high zinc content are prepared by ultrasonic spray pyrolysis and subsequent nitridation. The structure and morphology of the samples are investigated by X-ray diffraction (XRD), field-emission scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The characterization results show a phase transition from the Zn and Ga-based oxides (ZnO or ZnGa2O4) to a (GaN)1-x (ZnO)x solid solution under an NH3 atmosphere. The effect of the precursor solution concentration and nitridation temperature on the final products are systematically investigated to obtain (GaN)1-x(ZnO)x nanoparticles with a high Zn concentration. It is confirmed that the powder synthesized from the solution in which the ratio of Zn and Ga was set to 0.8:0.2, as the initial precursor composition was composed of about 0.8-mole fraction of Zn, similar to the initially set one, through nitriding treatment at 700oC. Besides, the synthesized nanoparticles exhibited the typical XRD pattern of (GaN)1-x(ZnO)x, and a strong absorption of visible light with a bandgap energy of approximately 2.78 eV, confirming their potential use as a hydrogen production photocatalyst.
Abstract
In this study, (GaN)1-x(ZnO)x solid solution nanoparticles with a high zinc content are prepared by ultrasonic spray pyrolysis and subsequent nitridation. The structure and morphology of the samples are investigated by X-ray diffraction (XRD), field-emission scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The characterization results show a phase transition from the Zn and Ga-based oxides (ZnO or ZnGa2O4) to a (GaN)1-x (ZnO)x solid solution under an NH3 atmosphere. The effect of the precursor solution concentration and nitridation temperature on the final products are systematically investigated to obtain (GaN)1-x(ZnO)x nanoparticles with a high Zn concentration. It is confirmed that the powder synthesized from the solution in which the ratio of Zn and Ga was set to 0.8:0.2, as the initial precursor composition was composed of about 0.8-mole fraction of Zn, similar to the initially set one, through nitriding treatment at 700oC. Besides, the synthesized nanoparticles exhibited the typical XRD pattern of (GaN)1-x(ZnO)x, and a strong absorption of visible light with a bandgap energy of approximately 2.78 eV, confirming their potential use as a hydrogen production photocatalyst.
참고문헌 (24)
- B. Liu, , Small, 13, pp.1701998~ (2017)
- L. W. Yin, , Nano Lett, 9, pp.957~ (2009)
- B. Liu, , Nano Lett, 13, pp.85~ (2013)
- J. N. Hart, , Adv. Mater, 25, pp.2989~ (2013)
- Z. Deng, , J. Am. Chem. Soc, 131, pp.17744~ (2009)
- Y. Wang, , Phys. Chem. Chem. Phys, 15, pp.2912~ (2013)
- K. Maeda, , J. Am. Chem. Soc, 127, pp.8286~ (2005)
- T. Hisatomi, , Chem. Soc. Rev, 43, pp.7520~ (2014)
- J. Kou, , J. Mol. Catal. A: Chem., 325, pp.48~ (2010)
- A. Wu, , Dalton Trans, 46, pp.2643~ (2017)
- K. Lee, , Nano Lett, 12, pp.3268~ (2012)
- C. H. Chuang, , J. Am. Chem. Soc, 137, pp.6452~ (2015)
- K. Lee, , J. Mater. Chem. A, 4, pp.2927~ (2016)
- J. Li, , Nanoscale, 8, pp.3694~ (2016)
- K. Maeda, , J. Catal, 254, pp.198~ (2008)
- Y. Asakura, , Eur. J. Inorg. Chem, 2019, pp.1999~ (2019)
- Y. -L. Hu, , Inorg. Chem, 59, pp.7012~ (2020)
- Y. Hwangbo, , J. Alloys Compd, 771, pp.821~ (2019)
- J. -H. Yoo, , J. Photochem. Photobiol. A: Chem., 401, pp.112782~ (2020)
- J. H. Bang, , Adv. Mater, 22, pp.1039~ (2010)
- 최요민, "Facile and Selective Synthesis of ZnO Hollow or Crumpled Spheres and Their Photocatalytic Degradation Activities", 한국세라믹학회지, 55(3), pp.261~266 (2018), 한국세라믹학회
- 지명준, "초음파 분무 열분해 공정과 질화처리를 이용한 GaN 분말의합성과 광학적 성질", 한국분말재료학회지, 25(6), pp.482~486 (2018), 한국분말재료학회[DOI]
- Z. Galazka, , APL Mater, 7, pp.022512~ (2019)
- P. Kubelka, , Z. Tech. Phys, 12, pp.59~ (1931)