습식화학공정에 의한 광촉매용 TiO2 3차원 나노구조체 제조 연구
Study on the Preparation of TiO2 3D Nanostructure for Photocatalyst by Wet Chemical Process
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this work, TiO2 3D nanostructures (TF30) were prepared via a facile wet chemical process using ammonium hexafluorotitanate. The synthesized 3D TiO2 nanostructures exhibited well-defined crystalline and hierarchical structures assembled from TiO2 nanorods with different thicknesses and diameters, which comprised numerous small beads. Moreover, the maximum specific surface area of TiO2 3D nanostructures was observed to be 191 m2g1, with concentration of F ions on the surface being 2 at%. The TiO2 3D nanostructures were tested as photocatalysts under UV irradiation using Rhodamine B solution in order to determine their photocatalytic performance. The TiO2 3D nanostructures showed a higher photocatalytic activity than that of the other TiO2 samples, which was likely associated with the combined effects of a high crystallinity, unique features of the hierarchical structure, a high specific surface area, and the advantage of adsorbing F ions.
Abstract
In this work, TiO2 3D nanostructures (TF30) were prepared via a facile wet chemical process using ammonium hexafluorotitanate. The synthesized 3D TiO2 nanostructures exhibited well-defined crystalline and hierarchical structures assembled from TiO2 nanorods with different thicknesses and diameters, which comprised numerous small beads. Moreover, the maximum specific surface area of TiO2 3D nanostructures was observed to be 191 m2g1, with concentration of F ions on the surface being 2 at%. The TiO2 3D nanostructures were tested as photocatalysts under UV irradiation using Rhodamine B solution in order to determine their photocatalytic performance. The TiO2 3D nanostructures showed a higher photocatalytic activity than that of the other TiO2 samples, which was likely associated with the combined effects of a high crystallinity, unique features of the hierarchical structure, a high specific surface area, and the advantage of adsorbing F ions.
참고문헌 (26)
- 이슬이, "TiO2 photocatalyst for water treatment applications", Journal of Industrial and Engineering Chemistry, 19(6), pp.1761~1769 (2013), 한국공업화학회
- M. N. Chong, , Water Res, 44, pp.2997~ (2010)
- M. Rawolle, , Small, 7, pp.884~ (2011)
- H. Y. Yin, , J. Alloys Compd, 640, pp.68~ (2015)
- W. Q. Fang, , Chem. Eur. J, 17, pp.1423~ (2011)
- X. F. Yang, , ACS Catal, 3, pp.363~ (2013)
- X. F. Guan, , J. Alloys Compd, 509, pp.3367~ (2011)
- Y. F. Tang, , Langmuir, 26, pp.10111~ (2010)
- C. X. Wang, , Langmuir, 26, pp.12841~ (2010)
- J. Zhu, , Res. Chem. Intermed, 35, pp.769~ (2009)
- J. Zhu, , Appl. Catal. B. Environ, 102, pp.120~ (2011)
- X. J. Lu, , Adv. Mater, 22, pp.3719~ (2010)
- D. C. Pan, , Adv. Mater, 17, pp.1991~ (2005)
- J. M. Macak, , Angew. Chem. Int. Ed, 44, pp.2100~ (2005)
- G. Wu, , Langmuir, 24, pp.3503~ (2008)
- T. Zhu, , ACS Appl. Mater. Interface, 3, pp.3448~ (2011)
- G. Tian, , Cryst. Eng. Comm, 13, pp.2994~ (2011)
- H. Li, , J. Alloys Compd, 657, pp.1~ (2016)
- Z. Wu, , Particuology, 15, pp.61~ (2014)
- H. Park, , J. Phys. Chem. B, 108, pp.4086~ (2004)
- W. Gan, , Phys. Status Solidi A, 213, pp.994~ (2016)
- Y. Fan, , Inter. J. Photoenergy, 2012, pp.1~ (2011)
- S. S. Ma, , J. Mater. Chem. A, 2, pp.7272~ (2014)
- J. G. Yu, , Adv. Funct. Mater, 17, pp.1984~ (2007)
- H. Li, , J. Alloys Compd, 657, pp.1~ (2016)
- M. A. Lara, , J. Mater. Sci, 53, pp.435~ (2018)