In this study, TiO2 powders are synthesized from ammonium hexafluoride titanate (AHFT, (NH4)2TiF6) as a precursor by heat treatment. First, we evaluate the physical properties of AHFT using X-ray diffraction (XRD), particle size analysis (PSA), thermogravimetric analysis (TGA), and field-emission scanning electron microscopy (FESEM). Then, to prepare the TiO2 powders, is heat-treated at 300-1300oC for 1 h. The ratio of anatase to rutile phase in TiO2 is estimated by XRD. The anatase phase forms at 500oC and phase transformation to the rutile phase occurs at 1200oC. Increase in the particle size is observed upon increasing the reaction temperature, and the phase ratio of the rutile phase is determined from a comparison with the calculated XRD data. Thus, we show that anatase and rutile TiO2 powders could be synthesized using AHFT as a raw material, and the obtained data are utilized for developing a new process for producing high-quality TiO2 powder.
Abstract
In this study, TiO2 powders are synthesized from ammonium hexafluoride titanate (AHFT, (NH4)2TiF6) as a precursor by heat treatment. First, we evaluate the physical properties of AHFT using X-ray diffraction (XRD), particle size analysis (PSA), thermogravimetric analysis (TGA), and field-emission scanning electron microscopy (FESEM). Then, to prepare the TiO2 powders, is heat-treated at 300-1300oC for 1 h. The ratio of anatase to rutile phase in TiO2 is estimated by XRD. The anatase phase forms at 500oC and phase transformation to the rutile phase occurs at 1200oC. Increase in the particle size is observed upon increasing the reaction temperature, and the phase ratio of the rutile phase is determined from a comparison with the calculated XRD data. Thus, we show that anatase and rutile TiO2 powders could be synthesized using AHFT as a raw material, and the obtained data are utilized for developing a new process for producing high-quality TiO2 powder.
참고문헌 (21)
- H. Chang, , Chem. Mater., 7, pp.663~ (1995)
- B. S. Lee, , J. Korean Ceram. Soc., 37, pp.308~ (2000)
- J. Yang, , J. American Ceramic Soc., 83, pp.1361~ (2000)
- 김정곤, "MAO 공정 변수가 TiO2 산화피막의 구조 및 광촉매 특성에 미치는 영향", 한국분말야금학회지, 19(3), pp.196~203 (2012), 한국분말야금학회[DOI]
- 박현수, "과산화 티타늄 복합체를 이용한 염료감응형 태양전지용 페이스트의 제조 및 열처리 온도에 따른 특성", 한국분말야금학회지, 22(6), pp.396~402 (2015), 한국분말야금학회
- L. Gao, , Materials Transactions, 42, pp.1676~ (2001)
- 최순옥, "황산법을 이용한 루틸형 TiO_2 분말의 제조 및 특성 평가", 대한금속·재료학회지, 50(7), pp.523~530 (2012), 대한금속·재료학회[DOI]
- J. H. Braun, , Prog. Org. Coat., 20, pp.105~ (1992)
- A. S. Attar, , J. Mater. Sci., 43, pp.1723~ (2008)
- H. Yin, , J. Mater. Chem., 11, pp.1694~ (2001)
- T. Sugimoto, , J. Colloid Interface Sci., 259, pp.53~ (2003)
- N. Venkatachalam, , Mater. Chem. Phys, 104, pp.454~ (2007)
- A. Y. Zhang, , Green Chem., 16, pp.2745~ (2014)
- H. J. Noh, , J. Kor. Ceram. Soc., 39 (2002)
- H. Nishzawa, , J. Am. Ceram. Soc., 65, pp.343~ (1982)
- S. D. Mo, , Phys. Rev. B, 51, pp.13023~ (1995)
- O. Carp, , Prog. Solid State Chem., 21, pp.33~ (2004)
- J. Kim, , J. Eur. Ceram. Soc., 21, pp.2863~ (2001)
- T. B. Ghosh, , J. Appl. Phys., 94, pp.4577~ (2003)
- M. Hirano, , J. Solid State Chem., 170, pp.39~ (2003)
- J. Arbiol, , J. Appl. Phys., 92, pp.85~ (2002)