TiO2 첨가량에 따른 Nd2O3, Yb2O3 첨가 YSZ 복합 소재의 고온 열화거동 분석
Effect of TiO2 Content on High-Temperature Degradation Behavior of Nd2O3 and Yb2O3–Doped YSZ Composite Materials
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Hot section components of gas turbines are exposed to a high operating temperature environment. To protect these components, thermal barrier coatings (TBC) are applied to their surfaces. Yttria-stabilized zirconia (YSZ), which is widely used as a TBC material, faces limitations at temperatures above 1200℃. To mitigate these issues, research has focused on adding lanthanide rare earth oxides and tetravalent oxides to prevent the phase-transformation of the monoclinic phase in zirconia. This study investigated the effects of varying TiO2 content in Nd2O3 and Yb2O3 co-doped YSZ composites. Increasing TiO2 content effectively suppressed formation of the monoclinic phase and increased the thermal degradation resistance compared to YSZ in environments over 1200℃. These findings will aid in developing more thermally stable and efficient TBC materials for application in high-temperature environments.
Abstract
Hot section components of gas turbines are exposed to a high operating temperature environment. To protect these components, thermal barrier coatings (TBC) are applied to their surfaces. Yttria-stabilized zirconia (YSZ), which is widely used as a TBC material, faces limitations at temperatures above 1200℃. To mitigate these issues, research has focused on adding lanthanide rare earth oxides and tetravalent oxides to prevent the phase-transformation of the monoclinic phase in zirconia. This study investigated the effects of varying TiO2 content in Nd2O3 and Yb2O3 co-doped YSZ composites. Increasing TiO2 content effectively suppressed formation of the monoclinic phase and increased the thermal degradation resistance compared to YSZ in environments over 1200℃. These findings will aid in developing more thermally stable and efficient TBC materials for application in high-temperature environments.
참고문헌 (22)
- R. A. Miller, , J. Therm. Spray Technol, 6, pp.35~ (1997)
- J. G. Thakare, , Met. Mater. Int, 27, pp.1947~ (2021)
- A. Feuerstein, , J. Therm. Spray Technol, 17, pp.199~ (2008)
- R. Vaßen, , Surf. Coat. Technol, 205, pp.938~ (2010)
- Q. Wei, , Thin Solid Films, 516, pp.5736~ (2008)
- Z. Shen, , Appl. Surf. Sci. Adv, 3, pp.100043~ (2021)
- E. V. Dudnik, , Powder Metall. Met. Ceram, 59, pp.179~ (2020)
- M. Bahamirian, , Ceram. Int, 45, pp.7344~ (2019)
- D. Chen, , Surf. Coat. Technol, 403, pp.126387~ (2020)
- M. Kibsey, , J. Eng. Gas Turbines Power, 133, pp.122101~ (2011)
- H. Jeon, , Ceram. Int, 48, pp.8177~ (2022)
- L. Guo, , Ceram. Int, 42, pp.7360~ (2016)
- J. Chevalier, , J. Am. Ceram. Soc, 92, pp.1901~ (2009)
- X. Ren, , Acta Mater, 69, pp.397~ (2014)
- T. A. Schaedler, , J. Am. Ceram. Soc, 90, pp.3896~ (2007)
- G. Witz, , J. Am. Ceram. Soc, 90, pp.2935~ (2007)
- M. T. Colomer, , J. Alloys. Compd, 689, pp.512~ (2016)
- L. Guo, , J. Eur. Ceram. Soc, 37, pp.4163~ (2017)
- T. Chen, , Ceram. Int, 34, pp.365~ (2008)
- M. Zhao, , Acta Mater, 61, pp.5496~ (2013)
- M. Zhao, , J. Am. Ceram. Soc, 97, pp.1566~ (2014)
- J. Gong, , Ceram. Int, 49, pp.37991~ (2023)