카본 코팅된 니켈-코발트 황화물의 요크쉘 입자 제조 및 소듐 이온 배터리의 음극 소재 적용
Synthesis of Carbon Coated Nickel Cobalt Sulfide Yolk-shell Microsphere and Their Application as Anode Materials for Sodium Ion Batteries
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Transition metal chalcogenides are promising cathode materials for next-generation battery systems, particularly sodium-ion batteries. Ni3Co6S8-pitch-derived carbon composite microspheres with a yolk-shell structure (Ni3Co6S8@C-YS) were synthesized through a three-step process: spray pyrolysis, pitch coating, and post-heat treatment process. Ni3Co6S8@C-YS exhibited an impressive reversible capacity of 525.2 mA h g-1 at a current density of 0.5 A g-1 over 50 cycles when employed as an anode material for sodium-ion batteries. However, Ni3Co6S8 yolk shell nanopowder (Ni3Co6S8-YS) without pitch-derived carbon demonstrated a continuous decrease in capacity during charging and discharging. The superior sodium-ion storage properties of Ni3Co6S8@C-YS were attributed to the pitchderived carbon, which effectively adjusted the size and distribution of nanocrystals. The carbon-coated yolk-shell microspheres proposed here hold potential for various metal chalcogenide compounds and can be applied to various fields, including the energy storage field.
Abstract
Transition metal chalcogenides are promising cathode materials for next-generation battery systems, particularly sodium-ion batteries. Ni3Co6S8-pitch-derived carbon composite microspheres with a yolk-shell structure (Ni3Co6S8@C-YS) were synthesized through a three-step process: spray pyrolysis, pitch coating, and post-heat treatment process. Ni3Co6S8@C-YS exhibited an impressive reversible capacity of 525.2 mA h g-1 at a current density of 0.5 A g-1 over 50 cycles when employed as an anode material for sodium-ion batteries. However, Ni3Co6S8 yolk shell nanopowder (Ni3Co6S8-YS) without pitch-derived carbon demonstrated a continuous decrease in capacity during charging and discharging. The superior sodium-ion storage properties of Ni3Co6S8@C-YS were attributed to the pitchderived carbon, which effectively adjusted the size and distribution of nanocrystals. The carbon-coated yolk-shell microspheres proposed here hold potential for various metal chalcogenide compounds and can be applied to various fields, including the energy storage field.
참고문헌 (26)
- M. Li, , Adv. Mater, 30, pp.1800561~ (2018)
- L. Deguenon, , J. Power Sources, 580, pp.233343~ (2023)
- T. Kim, , J. Mater. Chem. A, 7, pp.2942~ (2019)
- Y. Wang, , J. Power Sources, 286, pp.330~ (2015)
- C. Delmas, , Adv. Energy Mater, 8, pp.1703137~ (2018)
- J. -Y. Hwang, , Chem. Soc. Rev, 46, pp.3529~ (2017)
- C. Vaalma, , Nat. Rev. Mater, 3, pp.1~ (2018)
- C. Dong, , Small, 16, pp.2004580~ (2020)
- H. Liu, , ACS Appl. Mater. Interfaces, 8, pp.26878~ (2016)
- Y. Zhao, , Energy Storage Mater, 18, pp.51~ (2019)
- Z. Liu, , Energy Environ. Sci, 10, pp.1576~ (2017)
- G. K. Veerasubramani, , J. Mater. Chem. A, 6, pp.20056~ (2018)
- H. Tan, , Small Methods, 4, pp.1900563~ (2020)
- Z. Hao, , Adv. Funct. Mater, 32, pp.2208093~ (2022)
- Y. Gong, , Small, 19, pp.2206194~ (2023)
- G. Huang, , J. Power Sources, 235, pp.122~ (2013)
- S. Li, , Energy Storage Mater, 25, pp.636~ (2020)
- W. Chen, , J. Electroanal. Chem, 929, pp.117095~ (2023)
- M. Kim, , Int. J. Energy Res, 46, pp.5800~ (2022)
- C. Wu, , Nano-Micro Lett, 10, pp.1~ (2018)
- J. Liu, , Chem. Commun, 47, pp.12578~ (2011)
- Y. J. Hong, , Adv. Mater, 25, pp.2279~ (2013)
- D. S. Jung, , Adv. Powder Technol, 25, pp.18~ (2014)
- L. Zhang, , CompComm, 21, pp.100395~ (2020)
- J. H. Kim, , Int. J. Energy Res, 45, pp.14910~ (2021)
- X. Liu, , J. Alloys Compd, 854, pp.157132~ (2021)