초음파 분무 열분해법으로 제조한 텅스텐 분말의 상압소결과 미세조직
Pressureless Sintering and Microstructure of Pure Tungsten Powders Prepared by Ultrasonic Spray Pyrolysis
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
This study demonstrates the effect of the compaction pressure on the microstructure and properties of pressureless-sintered W bodies. W powders are synthesized by ultrasonic spray pyrolysis and hydrogen reduction using ammonium metatungstate hydrate as a precursor. Microstructural investigation reveals that a spherical powder in the form of agglomerated nanosized W particles is successfully synthesized. The W powder synthesized by ultrasonic spray pyrolysis exhibits a relative density of approximately 94% regardless of the compaction pressure, whereas the commercial powder exhibits a relative density of 64% under the same sintering conditions. This change in the relative density of the sintered compact can be explained by the difference in the sizes of the raw powder and the densities of the compacted green body. The grain size increases as the compaction pressure increases, and the sintered compact uniaxially pressed to 50 MPa and then isostatically pressed to 300 MPa exhibits a size of 0.71 m. The Vickers hardness of the sintered W exhibits a high value of 4.7 GPa, mainly due to grain refinement.
Abstract
This study demonstrates the effect of the compaction pressure on the microstructure and properties of pressureless-sintered W bodies. W powders are synthesized by ultrasonic spray pyrolysis and hydrogen reduction using ammonium metatungstate hydrate as a precursor. Microstructural investigation reveals that a spherical powder in the form of agglomerated nanosized W particles is successfully synthesized. The W powder synthesized by ultrasonic spray pyrolysis exhibits a relative density of approximately 94% regardless of the compaction pressure, whereas the commercial powder exhibits a relative density of 64% under the same sintering conditions. This change in the relative density of the sintered compact can be explained by the difference in the sizes of the raw powder and the densities of the compacted green body. The grain size increases as the compaction pressure increases, and the sintered compact uniaxially pressed to 50 MPa and then isostatically pressed to 300 MPa exhibits a size of 0.71 m. The Vickers hardness of the sintered W exhibits a high value of 4.7 GPa, mainly due to grain refinement.
참고문헌 (17)
- Y.-N. Liu, , J. Nucl. Mater, 455, pp.676~ (2014)
- K. Heinola, , J. Appl. Phys, 107, pp.113531~ (2010)
- L. J. Kecskes, , Metall. Mater. Trans. A, 26, pp.2407~ (1995)
- Z. Zhou, , Mater. Sci. Eng. A, 505, pp.131~ (2009)
- M. A. Monge, , J. Nucl. Mater, 386-388, pp.613~ (2009)
- J. M. Byun, , Int. J. Refract. Met. Hard Mater, 99, pp.105602~ (2021)
- I. H. Moon, , J. Le ss Common Met, 102, pp.219~ (1984)
- R. M. German, , Int. J. Refract. Met. Hard Mater, 23, pp.77~ (2005)
- P. Garg, , Int. J. Refract. Met. Hard Mater, 25, pp.16~ (2007)
- R. Malewar, , J. Mater. Res, 22, pp.1200~ (2007)
- 조현희, "초음파 분무 열분해법으로 제조한 텅스텐 미세분말의 미세조직과 소결 거동", 대한금속·재료학회지, 59(5), pp.289~294 (2021), 대한금속·재료학회[DOI]
- A. S. Abdallah, , J. Eng. Sci. Military Technol, 1, pp.17~146 (2017)
- 문환균, "기계적 합금화환( Al+12.5%Cu)3Zr 초미립 금속간화합물의 CIP 성형 및 소결 거동", 한국재료학회지, 12(8), pp.634~640 (2002), 한국재료학회
- Y. Wang, , High Temp. Mater. Process, 40, pp.171~ (2021)
- 권나연, "나노-마이크로 크기 하이브리드 구조 텅스텐 분말특성에 미치는 분말혼합 공정의 영향", 한국분말재료학회지, 24(5), pp.384~388 (2017), 한국분말재료학회[DOI]
- R. M. German, , Powder Metall, 49, pp.19~ (2006)
- Z. Z. Fang, , Int. Mater. Rev, 53, pp.326~ (2008)