확산한계전류밀도 고찰에 의한 방청도료의 내식성평가
Evaluation of Corrosion Resistance of Anti-Corrosive Paint by Investigation of Diffusion LimitingCurrent Density
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
It has been observed that coated steel structures deteriorate more rapidly than the designed lifetime due to acid rain caused by air pollution, etc. Therefore, improving the corrosion resistance of anti-corrosive paint is very important in terms of safety and the economic point of view. In this study, the corrosion resistance of five kinds of anti-corrosive paints, including the Acryl, Fluorine, and Epoxy resin series, were investigated with electrochemical methods, such as corrosion potential measurements, polarization curves, diffusion limiting current density, etc. As a result, the corrosion resistance of the F101 specimen with the fluorine resin series was found to be superior to the other specimens, while E100 with the epoxy resin series also showed a somewhat good corrosion resistance. Furthermore, it was observed that the amount of water and oxygen entering the inner side of a painted film increased with an increase in immersion time, irrespective of the kind of resin series. However, the oxygen diffusion limiting current density of a specimen with good corrosion resistance was relatively decreased compared to other specimens, because of the difficulty of oxygen diffusion penetrating to the inner side of the film. Consequently it is suggested that we can qualitatively evaluate the corrosion resistance of an anti-corrosive paint by measuring the diffusion limiting current density as an electrochemical method.
Abstract
It has been observed that coated steel structures deteriorate more rapidly than the designed lifetime due to acid rain caused by air pollution, etc. Therefore, improving the corrosion resistance of anti-corrosive paint is very important in terms of safety and the economic point of view. In this study, the corrosion resistance of five kinds of anti-corrosive paints, including the Acryl, Fluorine, and Epoxy resin series, were investigated with electrochemical methods, such as corrosion potential measurements, polarization curves, diffusion limiting current density, etc. As a result, the corrosion resistance of the F101 specimen with the fluorine resin series was found to be superior to the other specimens, while E100 with the epoxy resin series also showed a somewhat good corrosion resistance. Furthermore, it was observed that the amount of water and oxygen entering the inner side of a painted film increased with an increase in immersion time, irrespective of the kind of resin series. However, the oxygen diffusion limiting current density of a specimen with good corrosion resistance was relatively decreased compared to other specimens, because of the difficulty of oxygen diffusion penetrating to the inner side of the film. Consequently it is suggested that we can qualitatively evaluate the corrosion resistance of an anti-corrosive paint by measuring the diffusion limiting current density as an electrochemical method.
참고문헌 (14)
- Cicognami, P., "Application of the Boundary-element Method to Offshore Cathodic Protection Modeling", J. Electrochem. Soc., 137(6), pp.169~1695 (1990)
- Compton, K.G., "Factor Involved in Corrosion of Lead Cable Sheath", Corrosion, 17, pp.115~118 (1961)
- Gartland, P.O., "Effect of Flow on the Cathodic Protection of a Steel Cylinder in Sea Water", Corrosion, 40(3), pp.127~133 (1984)
- Hiramatsi, M., "Current Trend in Development of Corrosion Protective Plating", Zairoto-Kankyo, 45(1), pp.33~41 (1996)
- Jones, D.A., "Electrochemical Corrosion Studies on Zinc-coated Steel", Corrosion, 41(6), pp.357~362 (1985)
- Newman, J., "Cathodic Protection with Parrel Cylinders", J. Electrochem. Soc., 130(12), pp.3554~3559 (1991)
- Steinsmo,U.and Bardal,E, "Factors Limiting the Cathodic Current on Painted Steel", J. Electrochem. Soc., 136(12), pp.3588~3594 (1989)
- Steinsmo, U., "The Effect of the Dry Film Thickness, Temperature, and Electrolyte on the Cathodic Current of Painted Steel", J. Electrochem. Soc., 136(12), pp.3383~3587 (1989)
- Talati, J.D., "Maximum Utilization Current Density", Corrosion, 40(2), pp.88~91 (1984)
- The Overseas Coastal Area Development Institute of Japan, "Corrosion Protection and Repair Manual for Port and Harbor Steel Structures", pp.27~96 (1998)
- 문경만, "중방식 도료의 내식성에 미치는 첨가제의 영향", 한국해양공학회지, 21(3), pp.65~70 (2007), 한국해양공학회
- 문경만, "알기쉬운 문답식 실용전기화학", pp.106~148 (1999), 효성출판사
- 부식손실조사보고서, "일본방식기술협회", ~ (1977)
- 성호진, "중방식도료의 내식성에 관한 전기화학적 평가", 한국마린엔지니어링학회지, 29(5), pp.519~525 (2005), 한국마린엔지니어링학회