쇼트 피닝의 압력변화에 따른 A7075-T651재의 VHCF 피로특성
VHCF Characteristics of A7075-T651 under Pressure Variation by Shot Peening Treatment
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this paper, the fatigue characteristics of shot peened A7075-T651 alloy were compared with those of the specimens without the shot peening. The multi-spindle and single-spindle rotating bending fatigue testing machines were employed for the evaluation. Shot peening (SP)with various pressure (5 psi, 10 psi, 15 psi, 25 psi and 35 psi) were used in this test. In order to investigate the effect of the applied pressure during the SP, we carried out the surface roughness test, compressive residual stress test, hardness test, tensile test, VHCF (Very high cycle fatigue) test and SEM observation. SP induced the formation of remarkable compressive residual stress from the surface to certain depth of sample by means of the plastic deformation. The surface hardness and the fatigue characteristics of the specimens were also modified by the SP. According to the S-N curves, fatigue lives of shot peended sample with 25 psi measures 50 times higher than that of the untreated sample. The fatigue lives of shot peened sample with 15 psi and 35 psi measure approximately 10 times higher than that of the untreated ones.
Abstract
In this paper, the fatigue characteristics of shot peened A7075-T651 alloy were compared with those of the specimens without the shot peening. The multi-spindle and single-spindle rotating bending fatigue testing machines were employed for the evaluation. Shot peening (SP)with various pressure (5 psi, 10 psi, 15 psi, 25 psi and 35 psi) were used in this test. In order to investigate the effect of the applied pressure during the SP, we carried out the surface roughness test, compressive residual stress test, hardness test, tensile test, VHCF (Very high cycle fatigue) test and SEM observation. SP induced the formation of remarkable compressive residual stress from the surface to certain depth of sample by means of the plastic deformation. The surface hardness and the fatigue characteristics of the specimens were also modified by the SP. According to the S-N curves, fatigue lives of shot peended sample with 25 psi measures 50 times higher than that of the untreated sample. The fatigue lives of shot peened sample with 15 psi and 35 psi measure approximately 10 times higher than that of the untreated ones.
참고문헌 (20)
- Barsom, J.M, "Fracture and Fatigue Control in Structure", pp.163~192 (1999), Buttworth Heinemann
- Cheng, S.K, "Effect of the Peening Intensity by Shot peening", Transactions of the KSME, 25(10), pp.1590~1596 (2001)
- JIS Z 2274, "Method of Rotating Bending Fatigue Testing of Metals", ~
- Knott, J.F, "Fundamentals of Fracture Mechanics", pp.234~245 (1979), Collins and Co
- Lee, C.J, "Fatigue Properties of Aluminum Alloy (A6061-T6) with Ultrosonic Nano- Crystal Surface Modification", Journal of Modern Physics B, 24, pp.2512~2517 (2010)
- Pyun, Y.S, "Development of an Automated Super Surface Finishing System for the 3D Sculptured Surface of Model and Dies using Ultrasonic Micro Burnishing Technology", Processing of the 32nd ISR (2001)
- Sakai, T, "Effect of Stress Ratio on Long Life Fatigue Behavior of High Carbon Chromium Bearing Steel under Axial Loading", Int. J. of Fatigue 28, pp.1547~1554 (2006)
- Shiozawa, K, "Very High-Cycle Fatigue Behaviour of Shot-Peened High-Carbon-Chromium Bearing Steel", Fatigue & Fracture of Engineering Materials & Structure, 25(8), pp.813~822 (2002)
- Stephens, R.I, "Metal Fatigue in Engineering, Wiley interscience Pub", pp.59~89 (2001), Wiley interscience Pub
- Suh, C.M, "Fatigue Microcracks in a Low Carbon Steel", Fatigue Fract. Engng. Mater. Struct, 8(2), pp.193~203 (1985)
- Suh, C.M, "Crack Growth Behaviour of Fatigue Microcracks in Low Carbon Steels", Fatigue Fract. Engng. Mater, 9(6), pp.409~424 (1987)
- Suh, C.M, "Improvement of VHCF properties of AISI 1045, 4137, 52100 & H13 steel by UNSM treatment", 2011년도 한국해 양과학기술협의회 공동학술대회, pp.1574~1579 (2011)
- Suh, C.M, "Fatigue Characteristics of Nitrided SACM 645 according to the Nitriding Condition and Notch", Materials Science and Engineering A, 392, pp.31~37 (2005)
- Suh, C.M, "Fatigue and mechanical characteristics of nano-structured tool steel by ultrasonic cold forging technology", MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 443(1-2), pp.101~106 (2007), ELSEVIER SCIENCE SA
- Suh, C.M, "A Simulation of the Behavior of Multi-Surface Fatigue Crack in Type 304 Stainless Steel Plate", Fatigue Fract. Engng. Mater, 18(4), pp.515~525 (1995)
- Torres, M.A.S, "An Evaluation of Shot Peening, Residual Stress and Stress Relaxation on The Fatigue Life of AISI 4340 Steel", International Journal of Fatigue, 24(8), pp.877~886 (2002)
- Wanger, L, "Mechanical Surface Treatments on Titanium, Aluminum and Magnesium Alloys", Materials Science & Engineering, pp.263~270 (1999)
- Zhang, P, "Influence of Shot Peening on hIgh Cycle Fatigue Properties of The High- Strength Wrought Magnesium Alloy AZ80", Scripta materialia, 52(6), pp.485~490 (2005)
- 박경동, "쇼트피닝 가공된 해양구조용강의 피로파괴에 미치는 응력비의 영향", 한국해양공학회지, 18(5), pp.43~49 (2004), 한국해양공학회
- 심동석, "균열진전에 대한 쇼트피닝 효과", 한국해양공학회지, 18(6), pp.91~95 (2004), 한국해양공학회