셀프실드아크 용접금속의 확산성수소량에 미치는 용접변수의 영향
Effects of Welding Parameters on Diffusible Hydrogen Contents in FCAW‐S Weld Metal
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The effects of the welding parameters, contact tip‐to‐workpiece distance (CTWD), current, and voltage on the diffusible hydrogen content in weld metal deposited by self‐shielded flux cored arc welding were investigated and rationalized by comparing the amount of heat generated in the extension length of the wire. This showed that as CTWD increased from 15mm to 25mm, the amount of heat generated was increased from 71.1J to 174.8J, and the hydrogen content was decreased from 11.3mL/100g to 5.9mL/100 g. Even if little difference was observed in the amount of heat generated, the hydrogen content was increased with an increase in voltage because of the longer arc length. A regression analysis showed that the regression coefficient of voltage in self‐shielded flux cored arc welding is greater than that in CO2 arc welding. This implies that voltage control is more important in self‐shielded flux cored arc welding than in CO2 arc welding.
Abstract
The effects of the welding parameters, contact tip‐to‐workpiece distance (CTWD), current, and voltage on the diffusible hydrogen content in weld metal deposited by self‐shielded flux cored arc welding were investigated and rationalized by comparing the amount of heat generated in the extension length of the wire. This showed that as CTWD increased from 15mm to 25mm, the amount of heat generated was increased from 71.1J to 174.8J, and the hydrogen content was decreased from 11.3mL/100g to 5.9mL/100 g. Even if little difference was observed in the amount of heat generated, the hydrogen content was increased with an increase in voltage because of the longer arc length. A regression analysis showed that the regression coefficient of voltage in self‐shielded flux cored arc welding is greater than that in CO2 arc welding. This implies that voltage control is more important in self‐shielded flux cored arc welding than in CO2 arc welding.
참고문헌 (12)
- Boniszewski, T., "Self-Shielded Arc Welding" (1992), Abington Publishing
- Easterling, K., "Introduction to the Physical Metallurgy of Welding. 2nd Edition" (1992), Butterworth-Heinemann
- Dixon, B., "Effects of Welding Parameters on Weld Zone Toughness and Hardness in 690MPa Steel", Welding Journal, 74(4), pp.122s~132s (1995)
- Haeck, R., "Developing Consumables and Process for Work on Offshore Platforms", Welding & Metal Fabrication, 48(9), pp.441~449 (1980)
- 한동우, "FCAW에서 용접금속 확산성수소량에 미치는 용접변수 영향의 정량적 해석", 대한용접접합학회지, 28(2), pp.54~59 (2010), 대한용접접합학회
- Harwig, D., "Effects of Welding Parameters and Electrode Atmospheric Exposure on the Diffusible Hydrogen Content of Gas Shielded Flux Cored Arc Welds", Welding Journal, 78(9), pp.314s~321s (1999)
- Keeler, T., "Innershield Welding. Part 1 Development and Applications", Metal Construction, 13(11), pp.667~673 (1981)
- Keeler, T., "Innershield Welding. Part 2 Properties", Metal Construction, 13(12), pp.750~753 (1981)
- Kiefer, J., "Effects of Moisture Contamination and Welding Parameters on Diffusible Hydrogen", Welding Journal, 75(5), pp.155s~161s (1996)
- Pittrun, M., "The Effect of Welding Parameters on Levels of Diffusible Hydrogen in Weld Metal Deposited Using Gas Shielded Rutile Flux Cored Wires", 박사, pp.2004
- Rodergs, K., "Self-Shielded Flux Cored Arc Welding-The Route to Good Fracture Toughness", Welding Journal, 66(7), pp.49~59 (1987)
- White, D., "The Effect of Welding Parameters on Diffusible Hydrogen Levels in Cored Wire Welding", Welding & Metal Fabrication, 60(6), pp.209~216 (1992)