폴리머코어 게이트 크기 변화가 두께 방향 수축률에 미치는 영향에 대한 연구
A study on the effects of polymer core gate sizes on thickness shrinkage rate
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, the variation of the shrinkage in the thickness direction of the molded parts according to the gatesize of the polymer core fabricated through the 3D printer using the SLS method was studied. The polymer cores arelaser sintered and the powder material is nylon base PA2200. The polymer cores have lower heat transfer rate and rigiditythan the metal core due to the characteristics of the material. Therefore, the injection molding test conditions are set tominimize the deformation of the core during the injection process. The resin used in the injection molding test is a PPmaterial. The packing condition was set to 80, 90 and 100% of the maximum injection pressure for each gate size. Therunner diameter used was 3mm, and the gates were fabricated in semicircle shapes with cross sections 1, 2, and 3 mm2,respectively. Thickness measurement was performed for 10 points at 2.5 mm intervals from the point 2.5 mm away fromthe gate, and the shrinkage to thickness was measured for each point. The shrinkage rate according to the gate size tendsto decrease as the cross-sectional area decreases as the maximum injection pressure increases. The average thicknessshrinkage rate was close to 0% when the packing pressure was 90% for the gate area of 1mm2. When the holdingpressure was set to 100%, the shrinkage was found to decrease by 3% from the standard dimension due to theover-packing phenomenon. Therefore, the smaller the gate, the more closely the molded dimensions can be molded dueto the high pressure generation. It was confirmed that precise packing process control is necessary because over-packingphenomenon may occur.
Abstract
In this study, the variation of the shrinkage in the thickness direction of the molded parts according to the gatesize of the polymer core fabricated through the 3D printer using the SLS method was studied. The polymer cores arelaser sintered and the powder material is nylon base PA2200. The polymer cores have lower heat transfer rate and rigiditythan the metal core due to the characteristics of the material. Therefore, the injection molding test conditions are set tominimize the deformation of the core during the injection process. The resin used in the injection molding test is a PPmaterial. The packing condition was set to 80, 90 and 100% of the maximum injection pressure for each gate size. Therunner diameter used was 3mm, and the gates were fabricated in semicircle shapes with cross sections 1, 2, and 3 mm2,respectively. Thickness measurement was performed for 10 points at 2.5 mm intervals from the point 2.5 mm away fromthe gate, and the shrinkage to thickness was measured for each point. The shrinkage rate according to the gate size tendsto decrease as the cross-sectional area decreases as the maximum injection pressure increases. The average thicknessshrinkage rate was close to 0% when the packing pressure was 90% for the gate area of 1mm2. When the holdingpressure was set to 100%, the shrinkage was found to decrease by 3% from the standard dimension due to theover-packing phenomenon. Therefore, the smaller the gate, the more closely the molded dimensions can be molded dueto the high pressure generation. It was confirmed that precise packing process control is necessary because over-packingphenomenon may occur.
참고문헌 (7)
- Precision prototyping : The Role of 3D Printed Molds in the injection Molding Industry, "Zonder, L. L.", Stratasys Inc, ~ (2013)
- Kovacs, J. G, "Thermal simulations and measurements for rapid tool inserts in injection molding applications", Applied Thermal Engineering, 85, pp.44~51 (2015)
- Hassan, H., "Moldling the dffect of cooling system on the shrinkage and temperature of the polymer by injection molding", Applied Thermal Engineering, 30, pp.1547~1557 (2010)
- Marin, F., "Study of the design of cooling channels for polymers injection molds", Polymer Engineering and Science, 58, pp.552~559 (2017)
- Hassan, H., "3D study of cooling system effect on the heat transfer during polymer injection molding", Int. J. Therm, 49, pp.161~169 (2010)
- 조성우, "금형 게이트 크기 변화에 따른 멀티빔 센서용 렌즈 사출성형성 향상에 관한 연구", 소성∙가공, 20(5), pp.333~338 (2011), 한국소성∙가공학회
- 류민영, "성형조건과 수지의 종류에 따른 사출 성형품의 성형 수축", 엘라스토머 및 콤포지트, 38(4), pp.295~302 (2003), 한국고무학회