Polyethylene glycol이 3가크롬 전기도금에 미치는 효과
The Effect of Polyethylene glycol on the Trivalent Chromium Electroplating
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The effect of organic additives, polyethylene glycol (PEG), on the trivalent chromium electroplating was analysed in the view point of current efficiency, solution stability and metallurgical structure. It was measured that PEG-containing trivalent chromium solution had about 10% higher current effi-ciency than pure solution and controlled the micro-crack density of electrodeposits. PEG exhibited profound effect on the solution stability by reducing the consumption rate of formic acid which acts as a complexant to lower the activation energy required for electrochemical reduction of trivalent chro-mium ions. It was also revealed that the formation of chromium carbide layer was facilitated in the presence of polyethylene glycol, which meant easier electrochemical codeposition of chromium and carbon, not single chromium deposition. Trivalent chromium layer formed from PEG-containing solu-tion was amorphous with local nano-crystalline particles, which were prominently developed on the entire surface after non-oxidative heat treatment
Abstract
The effect of organic additives, polyethylene glycol (PEG), on the trivalent chromium electroplating was analysed in the view point of current efficiency, solution stability and metallurgical structure. It was measured that PEG-containing trivalent chromium solution had about 10% higher current effi-ciency than pure solution and controlled the micro-crack density of electrodeposits. PEG exhibited profound effect on the solution stability by reducing the consumption rate of formic acid which acts as a complexant to lower the activation energy required for electrochemical reduction of trivalent chro-mium ions. It was also revealed that the formation of chromium carbide layer was facilitated in the presence of polyethylene glycol, which meant easier electrochemical codeposition of chromium and carbon, not single chromium deposition. Trivalent chromium layer formed from PEG-containing solu-tion was amorphous with local nano-crystalline particles, which were prominently developed on the entire surface after non-oxidative heat treatment
참고문헌 (16)
- Y. B. Song, , Plat. Surf. Fin, 87(9), pp.80~ (2000)
- F. I. Danilov, , Protec. of Met, 42(6), pp.560~ (2006)
- Z. Zeng, , Electrochem. Commun, 11, pp.331~ (2009)
- J.-Y. Lee, , Nonferrous Met. Soc. China, 19, pp.819~ (2009)
- Z. V. Feng, , J. Phys. Chem. B, 107, pp.9415~ (2003)
- 이주열, "3가크롬 이온의 전착 반응에 용액 산도 및 유기물 첨가제가 미치는 영향 연구", 한국표면공학회지, 43(6), pp.297~303 (2010), 한국표면공학회
- S. K. Ibrahim, , Trans IMF, 75(5), pp.181~ (1997)
- 이철태, "유기 착화제의 형태에 따른 3가 크롬 전착 특성", 공업화학, 14(7), pp.959~967 (2003), 한국공업화학회
- Z. Zeng, , J. Zhang, Electrochem. Comm., 11, pp.331~ (2009)
- L. N. Vykhodtseva, , Russian J. Electrochem, 40, pp.387~ (2004)
- G. B. Hoflund, , J. Vac. Sci., Technol., 4, pp.26~ (1986)
- D. M. Brewis, , Polymer, 22, pp.7~ (1981)
- F. Ebrahimi, , Nanostruct. Mater, 11(3), pp.343~ (1999)
- Y. F. Shen, , Appl. Surf. Sci., 256(3), pp.710~ (2009)
- C. K. Chung, , Microsyst. Technol, 13, pp.537~ (2006)
- X. Yuan, , Surf. Coat. Technol., 202, pp.1895~ (2008)