CGL 층으로 MoOx를 사용한 다중 적층구조 OLED의 발광 특성
Emission Characteristics of Multi-Tandem OLED using MoOx with CGL
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
We studied emission characteristics of blue fluorescent multi-tandem OLEDs using Al/MoOx as charge generation layer(CGL). Threshold voltage for 2, 3, 4, and 5 units tandem OLEDs was 8, 11, 14 and 18 V, respectively. The threshold voltage in multi-tandem OLEDs was lower than multiple of 4 V for the single OLED. Maximum current efficiency and maximum quantum efficiency of single OLED were 7.6 cd/A and 5.5%. Maximum current efficiency for 2, 3, 4, and 5 units tandem OLEDs was 22.6, 31.4, 41.2, and 46.6 cd/A, respectively. Maximum quantum efficiency for 2, 3, 4, and 5 units tandem OLEDs was 11.8, 15.8, 21.8, and 25.6%, respectively. The maximum current efficiency and maximum quantum efficiency in multi-tandem OLEDs were higher than multiple of those for the single OLED. The intensity for 508 nm peak was changed and the peak wavelength was red shift by increase of tandem unit in electroluminescent emission spectra. These phenomena can be caused by micro-cavity effect with increasing of organic layer thickness.
Abstract
We studied emission characteristics of blue fluorescent multi-tandem OLEDs using Al/MoOx as charge generation layer(CGL). Threshold voltage for 2, 3, 4, and 5 units tandem OLEDs was 8, 11, 14 and 18 V, respectively. The threshold voltage in multi-tandem OLEDs was lower than multiple of 4 V for the single OLED. Maximum current efficiency and maximum quantum efficiency of single OLED were 7.6 cd/A and 5.5%. Maximum current efficiency for 2, 3, 4, and 5 units tandem OLEDs was 22.6, 31.4, 41.2, and 46.6 cd/A, respectively. Maximum quantum efficiency for 2, 3, 4, and 5 units tandem OLEDs was 11.8, 15.8, 21.8, and 25.6%, respectively. The maximum current efficiency and maximum quantum efficiency in multi-tandem OLEDs were higher than multiple of those for the single OLED. The intensity for 508 nm peak was changed and the peak wavelength was red shift by increase of tandem unit in electroluminescent emission spectra. These phenomena can be caused by micro-cavity effect with increasing of organic layer thickness.
참고문헌 (17)
- C. W. Tang, , Appl. Phys. Lett, 51, pp.913~ (1987)
- J. Clark, , Nature, 4, pp.438~ (2010)
- T. Tsutsui, , Appl. Phys. Lett, 84, pp.440~ (2004)
- T. Tsutsui, , Appl. Phys. Lett, 90, pp.083502~ (2007)
- Fawen Guo, , Appl. Phys. Lett, 87, pp.173510~ (2005)
- Ping Chen, , Appl. Phys. Lett, 91, pp.023505~ (2007)
- P. S. Vincentt, , Thin Solid Film, 94, pp.171~ (1982)
- R. H. Partridge, , Polymer, 24, pp.748~ (1983)
- C. W. Tang, , Appl. Phys. Lett, 51, pp.913~ (1987)
- T. Chiba, , Organic Electronics, 12, pp.710~ (2011)
- 곽태호, "MoOx를 사용한 청색 형광 Tandem OLED의 발광 특성", 한국표면공학회지, 47(3), pp.104~108 (2014), 한국표면공학회[DOI]
- M. Liu, , Microelectronics Journal, 39, pp.1622~ (2008)
- C. H. Chang, , Thin Solid Films, 548, pp.389~ (2013)
- T. Chib, , Organic Electronics, 12, pp.710~ (2011)
- Peng, H., , Appl. Phys. Lett, 88, pp.073517~ (2006)
- Wu, C. C., , Appl. Phys. Lett, 84, pp.3966~ (2004)
- Chang, C. -H., , Org. Electron, 11, pp.247~ (2010)