CGL의 재료에 따른 청색 형광 Tandem OLED의 발광 특성
Emission Characteristics of Blue Fluorescence Tandem OLED with Materials of CGL
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
We investigated emission characteristics of tandem organic light emitting devices (OLEDs) with p-type materials as charge generation layer. The tandem OLEDs were fabricated by using MoOx, WOx, C60 and HATCN as p-type material or not using p-type material for charge generation. When HATCN was used as p-type material, it showed high current density at low applied voltage, but increase of efficiency was small because of charge unbalance in emitting layer. In case of tandem OLED not using p-type material, applied voltage increased remarkably because of difficulty of hole injection. In case of MoOx, WOx or C60 as ptype material, current emission efficiency increased greatly. In particular, current emission efficiency of tandem OLED using MoOx as p-type material increased up to 3 times than current emission efficiency of single OLED. The Commission Internationale de l’Eclairage (CIE) 1931 color coordinates were changed by overlapping of 504 nm emission wavelength. As a result, emission efficiency of tandem OLED improved compared with single OLED, but driving voltage also increased by increase of organic layer thickness.
Abstract
We investigated emission characteristics of tandem organic light emitting devices (OLEDs) with p-type materials as charge generation layer. The tandem OLEDs were fabricated by using MoOx, WOx, C60 and HATCN as p-type material or not using p-type material for charge generation. When HATCN was used as p-type material, it showed high current density at low applied voltage, but increase of efficiency was small because of charge unbalance in emitting layer. In case of tandem OLED not using p-type material, applied voltage increased remarkably because of difficulty of hole injection. In case of MoOx, WOx or C60 as ptype material, current emission efficiency increased greatly. In particular, current emission efficiency of tandem OLED using MoOx as p-type material increased up to 3 times than current emission efficiency of single OLED. The Commission Internationale de l’Eclairage (CIE) 1931 color coordinates were changed by overlapping of 504 nm emission wavelength. As a result, emission efficiency of tandem OLED improved compared with single OLED, but driving voltage also increased by increase of organic layer thickness.
참고문헌 (14)
- C. W. Tang, , Appl. Phys. Lett, 51, pp.913~ (1987)
- J. Clark, , Nature, 4, pp.438~ (2010)
- T. Tsutsui, , Appl. Phys. Lett, 84, pp.440~ (2004)
- T. Tsutsui, , Appl. Phys. Lett, 90, pp.083502~ (2007)
- Fawen Guo, , Appl. Phys. Lett, 87, pp.173510~ (2005)
- Ping Chen, , Appl. Phys. Lett, 91, pp.023505~ (2007)
- Hongmei Zhang, , Appl. Phys. Lett, 91, pp.123504~ (2007)
- Chieh-Wei Chen, , Appl. Phys. Lett, 87, pp.241121~ (2005)
- H. Kanno, , Adv. Mater, 18, pp.339~ (2006)
- Mei-Yee Chan, , Adv. Funct. Mater, 17, pp.2509~ (2007)
- T. Chib, , Nature, 347, pp.539~ (1990)
- 곽태호, "MoOx를 사용한 청색 형광 Tandem OLED의 발광 특성", 한국표면공학회지, 47(3), pp.104~108 (2014), 한국표면공학회[DOI]
- M. Liu, , Microelectronics Journal, 39, pp.1622~ (2008)
- C. H. Chang, , Thin Solid Films, 548, pp.389~ (2013)