알루미늄 6061-T6 합금에 대한 양극산화층이 해수 내 부식 및 응력부식균열에 미치는 영향
Effect on Anodizing Oxide Film for Aluminum 6061-T6 Alloy on Corrosion and Stress Corrosion Cracking in Seawater
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
This paper investigated the characteristics of anodized aluminum 6061-T6 alloy for corrosion and stress corrosion cracking(SCC) under natural seawater. The hard anodizing oxide film formed on the 6061-T6 was a uniform thickness of about 25 μm. The corrosion characteristics were performed with a potentiodynamic polarization test. SCC was characterized by a slow strain rate tensile test under 0.005mm/min rate. As a result, the anodizing film showed no significant effect on SCC in the slow strain rate test. However, the corrosion current density of base metal was measured to be approximately 13 times higher than that of the anodized specimen. Therefore, the anodizing film significantly improved the corrosion resistance of 6061-T6 alloy in natural seawater.
Abstract
This paper investigated the characteristics of anodized aluminum 6061-T6 alloy for corrosion and stress corrosion cracking(SCC) under natural seawater. The hard anodizing oxide film formed on the 6061-T6 was a uniform thickness of about 25 μm. The corrosion characteristics were performed with a potentiodynamic polarization test. SCC was characterized by a slow strain rate tensile test under 0.005mm/min rate. As a result, the anodizing film showed no significant effect on SCC in the slow strain rate test. However, the corrosion current density of base metal was measured to be approximately 13 times higher than that of the anodized specimen. Therefore, the anodizing film significantly improved the corrosion resistance of 6061-T6 alloy in natural seawater.
참고문헌 (16)
- J. R, Davis, "Corrosion of aluminum and aluminum alloys" (1999), ASM International
- H. Ezuber, "study on the corrosion behavior of aluminum alloys in seawater", Mater. Design, 29(4), pp.801~805 (2008)
- 박일초, "알루미늄 합금 및 스테인리스강의 해수 농도 변화에 따른 전기화학적 부식 손상 특성", 한국표면공학회지, 50(4), pp.259~265 (2017), 한국표면공학회[DOI]
- M. Liang, "Complex Pitting Corrosion in Long-Term Immersed Exposures of 6060 Aluminum Alloys in Temperate Natural Seawater", Corrosion, 74(11), pp.1272~1287 (2018)
- L. Bouchama, "Enhancing aluminum corrosion resistance by two-step anodizing process", Surf. Coat. Tech., 235, pp.676~684 (2013)
- 박일초, "양극산화 후 실링처리된 알루미늄 합금의 해수 내 내식성과 캐비테이션 침식 저항성 평가", 한국표면공학회지, 51(2), pp.87~94 (2018), 한국표면공학회[DOI]
- L. Chen, "Influence of a MAO+PLGA coating on biocorrosion and stress corrosion cracking behavior of a magnesium alloy in a physiological environment", Corros. Sci., 148, pp.134~143 (2019)
- "ASTM E8", E8M-13a, Standard test methods for tension testing of metallic materials, 2013
- 문성모, "금속의 양극산화처리 기술", 한국표면공학회지, 51(1), pp.1~11 (2018), 한국표면공학회[DOI]
- D. Chen, "Corrosion of aluminium in the aqueous chemical environment of a loss of coolant accident at a nuclear power plant", Corros. Sci., 50(4), pp.1046~1057 (2008)
- 류한웅, "Al 6061 합금 양극산화피막의 성장과 부식특성에 미치는 혼합 전해용액의 영향", 한국재료학회지, 17(5), pp.244~249 (2007), 한국재료학회
- 이승준, "경금속 표면개질 시 황산 수용액 조건에 따른 내식성 개선 효과", 한국마린엔지니어링학회지, 39(3), pp.223~229 (2015), 한국마린엔지니어링학회[DOI]
- A. Yabuki, "Porous anodic oxide film with self-healing ability for corrosion protection of aluminum", Electrochim. Acta, 296, pp.662~668 (2019)
- 장일호, "질산가스분위기에서 황산 양극산화 피막처리된 Al6070 합금의 부식특성", 한국표면공학회지, 45(5), pp.198~205 (2012), 한국표면공학회[DOI]
- A. Venugopal, "Corrosion and nanomechanical behaviors of plasma electrolytic oxidation coated AA7020-T6 aluminum alloy", Mater. Sci. Eng. : A, 660, pp.39~46 (2016)
- X. Ji, "Strain-rate effect on work-hardening behavior in β-type Ti-10Mo-1Fe alloy with TWIP effect", Mater. Sci. Eng. : A, 707, pp.701~707 (2017)