LaCl3- CsCl 2성분계 용융염의 점도
Viscosities of LaCl3 - CsCl Binary Melts
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Viscosities of LaCl3-CsCl binary melts were measured by the capillary method over the range of their liquidus temperatures to about 1200 K. The cell constant were determined by using pure water. The results obtained are summerized as follows: Viscosities of melted LaCl3 were decreased with the content of CsCl for all over the composition range of binary melts. Composition versus viscosity relation for the binary melt showed a non-linear relationship from the additivity line and the deviations showed a maximum value at about 60 mol% CsCl. This suggest the existence of the complex ion of LaCl4− in the melt. Activation energy for the viscous flow of the binary melts decreased monotonously with the increasing content of CsCl after a few increasement till 40 mol% CsCl. All of these results were the resemble with the viscosities of LaCl3-NaCl binary melts.
Abstract
Viscosities of LaCl3-CsCl binary melts were measured by the capillary method over the range of their liquidus temperatures to about 1200 K. The cell constant were determined by using pure water. The results obtained are summerized as follows: Viscosities of melted LaCl3 were decreased with the content of CsCl for all over the composition range of binary melts. Composition versus viscosity relation for the binary melt showed a non-linear relationship from the additivity line and the deviations showed a maximum value at about 60 mol% CsCl. This suggest the existence of the complex ion of LaCl4− in the melt. Activation energy for the viscous flow of the binary melts decreased monotonously with the increasing content of CsCl after a few increasement till 40 mol% CsCl. All of these results were the resemble with the viscosities of LaCl3-NaCl binary melts.
참고문헌 (14)
- W. Klemm, , Z. Anorg. Allg. Chem, 152, pp.225~ (1926)
- W. Klemm, , Z. Anorg. Allg. Chem, 152, pp.267~ (1926)
- K. Cho, , Japanese J. Electrochemistry, 40, pp.45~ (1972)
- E. N. C. Andrade, , Proc. Roy. Soc., A211, pp.12~ (1952)
- H. R. Thersch, , Trans. Am. Soc. Metals, 55, pp.790~ (1962)
- M. R. Hopkins, , Proc. Phys. Soc., B63, pp.1773~ (1950)
- Moria, , Tetsu to Hagane, 56, pp.1613~ (1970)
- T. Ejima, , Japanese J. Chemistry, 6, pp.961~ (1982)
- T. Kinoshita, , Japanese J. Eng. Chem, 6, pp.961~ (1958)
- 김기호, "LaCl3 - NaCl 2성분계 용융염의 점도", 한국표면공학회지, 39(6), pp.282~287 (2006), 한국표면공학회
- K. Kim, , Japanese J. Metals, 51(7), pp.630~ (1987)
- E. N. C. Andrade, , Philos. Mag, 17(497), pp.698~ (1943)
- H. Kotama, , 석사, pp.1985
- "日本化學會便編覽 : 化學便覽(基礎編)", pp.505~ (1966), 丸善