기계적/전기화학적 표면처리가 알루미늄-에폭시의 접합강도 향상에 미치는 영향
Effect of Mechanical and Electrochemical Surface Treatments on Aluminium-Epoxy Adhesive Strength
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Low melting metals are difficult to weld because it is vaporized. But epoxy resin make bonding possible using low melting material and dismissal materials. This study is to improve the bonding strength of epoxy and substrate by mechanical and electrochemical methods. In case of mechanical work, bonding strength is 17.6MPa and in case of pre-work, bonding strength is 15.3MPa. When anodizing and mechanical work is applied, bonding strength is 25.3Mpa is increased 165%. When anodizing is applied, bonding strength is 27.6Mpa.
Abstract
Low melting metals are difficult to weld because it is vaporized. But epoxy resin make bonding possible using low melting material and dismissal materials. This study is to improve the bonding strength of epoxy and substrate by mechanical and electrochemical methods. In case of mechanical work, bonding strength is 17.6MPa and in case of pre-work, bonding strength is 15.3MPa. When anodizing and mechanical work is applied, bonding strength is 25.3Mpa is increased 165%. When anodizing is applied, bonding strength is 27.6Mpa.
참고문헌 (16)
- Jun Hee Song, "Bonding Strength in Structural Adhesive Bonded Joint", Met. Mater. Int, 7, pp.467~470 (2001)
- 김영식, "금속과 플라스틱의 최신접합기술", 대한용접접합학회지, 34(3), pp.31~39 (2016), 대한용접접합학회[DOI]
- E. Juntunen, "Thermal Performance Comparison of Thick-Film Insulated Aluminum Substrate With Metal Core PCBs for High-Power LED Modules", IEET. T. Compon, Pack. Man, 2, pp.1957~1964 (2012)
- E. Juntunen, "Copper-Core MCPCB with Thermal Vias for High-Power COB LED Modules", IEET. T. Power. Electr, 29, pp.1410~1417 (2014)
- W. K. C. Yung, "Using Metal Core Printed Circuit Board(MCPCB) as a Solution for Thermal Management", J. HKPCA, Q2, pp.12~16 (2007)
- T. P. Hoar, "A MECHANISM FOR THE FORMATION OF POROUS ANODIC OXIDE FILMS ON ALUMINIUM", J. Phys. Chem. Solids, 9, pp.97~99 (1959)
- S. Mohagheghi, "Effect of H3PO4 anodizing variations on Al-epoxy adhesion strength", Surf. Eng, 29, pp.737~742 (2013)
- D. E. Packham, "Mechanical factors in the adhesion of polyethylene to aluminum", J. Appl. Polym. Sci, 18, pp.3237~3247 (1974)
- A. Belwalkar, "Effect of Processing Parameters on Pore Structure and Thickness of Anodic Aluminum Oxide (AAO) Tubular Membranes", J. Membrane. Sci, 319, pp.192~198 (2008)
- J. -C. K. Woo Lee, "Spontaneous Current Oscillations during Hard Anodization of Aluminum under potentiostatic Conditions", Adv. Funct. Mater, 40, pp.21~27 (2010)
- L. Zaraska, "The effect of n-alcohols on porous anodic alumin formed by self-organized two-step anodizing of aluminum in phosphoric acid", Surf. Coat. Tech, 204, pp.1729~1737 (2010)
- 이슬기, "Effect of Aluminum Anodizing in Phosphoric Acid Electrolyte on Adhesion Strength and Thermal Performance", Metals and Materials International, 22(1), pp.20~25 (2016), 대한금속·재료학회[DOI]
- J. -S. Zhang, "The bonding strength and corrosion resistance of aluminum alloy by anodizing treatment in a phosphoric acid modified boric acid", sulfuric acid bath, 2008, pp.202, 3149~3156
- R. P. Digby, "Pretreatment of aluminum: topography, surface chemistry and adhesive bond durability", Int. J. Adhes. Adhes, 15, pp.61~71 (1995)
- O. Lunder, "Pretreatment of AA6060 aluminium alloy for adhesive bonding", Int. J. Adhes. Adhes, 22, pp.143~150 (2002)
- S. H. Han, "Effects of Pretreatment on the Adhesive Bonding of Aluminium Plate", J. Kor. Inst. Surf. Eng, 25, pp.97~102 (1992)