The Stability of Plating Solution and the Current Density Characteristics of the Sn-Ag Plating for the Wafer Bumping
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, the effects of the concentration of metal ions and the applied current density in the Sn-Ag plating solutions were examined in regards to the resulting composition and morphology of the solder bumps’ surface. Furthermore the effect of any impurities present in the methanesulfonic acid used as a base acid in the Sn-Ag solder plating solution on the stability of plating solution as well as the characteristics of the Sn-Ag alloys films was also explored. As expected, the uniform bump was obtained by means of removing impurities in the plating solution. Consequently the resultant solder bump was obtained in an optimal current density of the range of 1 A/dm2 to 15 A/dm2, which has acceptable bump shape and surface roughness with 12inch wafer trial results.
Abstract
In this study, the effects of the concentration of metal ions and the applied current density in the Sn-Ag plating solutions were examined in regards to the resulting composition and morphology of the solder bumps’ surface. Furthermore the effect of any impurities present in the methanesulfonic acid used as a base acid in the Sn-Ag solder plating solution on the stability of plating solution as well as the characteristics of the Sn-Ag alloys films was also explored. As expected, the uniform bump was obtained by means of removing impurities in the plating solution. Consequently the resultant solder bump was obtained in an optimal current density of the range of 1 A/dm2 to 15 A/dm2, which has acceptable bump shape and surface roughness with 12inch wafer trial results.
참고문헌 (12)
- H. Tong, "Advanced Flip Chip Packaging", pp.53~84 (2013), Springer
- J Busby, "C4NP Lead Free Solder Bumping and 3D Micro Bumping", IEEE, 2008, 333~339
- Manfred Jordan, "Lead-free Tin Alloys as Substitutes for Tin-lead Alloy Plating", The International Journal of Surface Engineering and Coatings, 75, pp.149~153 (1997)
- H. MORIUCHI, "Approach for External Stress Type Whisker Mitigation", J. Sur. Fin. Soc. Japan, 59, pp.218~222 (2008)
- B. L. Huang, "Prospects of Lead Free Alternatives for Reflow Soldering", Proc. of IMAPS'99, pp.13~ (1999)
- J. S. Ha, "Microstructure and Mechanical Properties of Partial Melted Joint Using off Eutectic Lead-free Solders", Mater. Trans, 42, pp.814~819 (2001)
- P. -Y. Chevalier, "A Thermodynamic Evaluation of the Ag-Sn system", Thermochim. Acta, 136, pp.45~54 (1988)
- K. S. Kim, "Effects of Intermetallic Compounds on Properties of Sn-Ag-Cu Lead-free Soldered Joints", J. Alloys and Compounds, 352, pp.226~236 (2003)
- E. P. Wood, "In Search of New Lead-free Electronic Solders", J. Electronic Mat, 23, pp.709~713 (1994)
- K. N. Subramanian, "Lead-Free Electronic Solder", pp.19~37 (2006), Springer
- Principles of Plating and the Plating Equipment, "H.Ryu", Korean Institute of Surface Engineering, 130~135 (2014)
- H. W. Chiang, "The Effect of Ag Content on the Formation of Ag3Sn Plates in Sn-Ag-Cu Lead-free Solder", J. Electronic Mat, 35, pp.2074~2080 (2006)