수명을 향상시키기 위해 Al 메탈 코팅과 양극산화처리된Steel 도가니의 파괴 거동
Fracture Behavior of Fe Crucible in Molten Aluminum Coated with Al and Anodized Al
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Steel crucible used for molten Al has a problem of very limited lifetime because of the interaction between Fe and molten Al. This study was performed to improve the lifetime of steel crucible for molten Al by coating metallic Al and by further anodizing treatment to form thick and uniform anodic oxide films. The lifetime of the steel crucible was improved slightly by Al coating from 30 to 40 hours by metallic Al coating and largely to 120 hours by coating the surface with anodic oxide film. The improved lifetime was attributed to blocking of the reaction between Fe and molten Al with the help of anodic oxide layer with more than 20 um thickness on the crucible surface. The failure of the steel crucible arises from the formation of intermetallic compounds and pores at the steel/Al interface.
Abstract
Steel crucible used for molten Al has a problem of very limited lifetime because of the interaction between Fe and molten Al. This study was performed to improve the lifetime of steel crucible for molten Al by coating metallic Al and by further anodizing treatment to form thick and uniform anodic oxide films. The lifetime of the steel crucible was improved slightly by Al coating from 30 to 40 hours by metallic Al coating and largely to 120 hours by coating the surface with anodic oxide film. The improved lifetime was attributed to blocking of the reaction between Fe and molten Al with the help of anodic oxide layer with more than 20 um thickness on the crucible surface. The failure of the steel crucible arises from the formation of intermetallic compounds and pores at the steel/Al interface.
참고문헌 (8)
- K. K. Fung, "Icosahedrally Related Decagonal Quasicrystal in Rapidly Cooled A1-14-at.%-Fe Alloy", Phys, Rev. Lett., 56, pp.2060~2063 (1986)[DOI]
- ON. Senkov, "Microstructure and Microhardness of an AI-Fe Alloy Subjected to Severe Plastic Deformation and Aging", Nanostruct. Mater, 10, pp.691~698 (1998)[DOI]
- T.T. Sasaki, "Microstructure and Mechanical Properties of Bulk Nanocrystalline Al-Fe Alloy Processed by Mechanical Alloying and Spark Plasma Sintering", Acta Mater., 57, pp.3529~3538 (2009)[DOI]
- Qin Jingyu, "Pre-peak in the structure factor of liquid Al-Fe alloy", J. Phys.: Condens. Matter., 10, pp.1211~1218 (1998)[DOI]
- T.T. Sasaki, "A High-Strength Bulk Nanocrystalline Al-Fe Alloy Processed by Mechanical Alloying and Spark Plasma Sintering", Scripta Mate., 57, pp.189~192 (2007)[DOI]
- R. KAINUMA, "Thermoelastic Martensite and Shape Memory Effect in B2 Base Ni-AI-Fe Alloy with Enhanced Ductility", Metall. Trans. A., 23, pp.1147~1153 (1992)[DOI]
- 정원섭, "기계적", 전기화학적 표면처리가 알루미늄-에폭시의 접합강도 향상에 미치는 영향, 2016, pp.49(6), 549~554[DOI]
- M. Gremaud, "Banding Phenomena in Ai-Fe Alloys Subjected To laser Surface Treatment", Acta Metall. Mater., 39, pp.1431~1443 (1991)[DOI]