알루미늄 2024 합금의 플라즈마 전해산화 피막의 형성 거동 및 피막 물성에 미치는 인산나트륨 농도의 영향
Effect of Na3PO4 Concentration on the Formation Behavior and Properties of PEO Films on AA2024
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
Formation behavior and properties of PEO (Plasma Electrolytic Oxidation) film on AA2024 were investigated under application of pulsed current as a function of Na3PO4 concentration in 0.05 M Na2SiO3 solution by analyzing voltage–time behavior, in-situ observation of arc generation, observation of surface morphology and measurements of thickness and surface roughness. Arc generation voltage decreased with increasing Na3PO4 concentration. Color difference of PEO films between edge and inner part disappeared by addition of Na3PO4. It was also observed that size of nodules on PEO film decreased with increasing Na3PO4 concentration. Thickness of PEO films formed on AA2024 increased with increasing Na3PO4 concentration. Whereas, surface roughness of PEO films decreased with increasing Na3PO4 concentration up to 0.05 M of Na3PO4 which is attributed to the deceased size of nodules on the PEO films. However, the surface roughness increased with increasing Na3PO4 concentration more than 0.07 M of Na3PO4 which seems to be due to the formation of non-uniform PEO films with smooth surface and large size pores formed by orange-colored big arcs. The experimental results suggest that added sodium phosphate less than 0.2 M in an alkaline silicate solution can contribute to the formation of relatively thick and uniform thickness of PEO films under arc generation voltage lower than 300 V.
Abstract
Formation behavior and properties of PEO (Plasma Electrolytic Oxidation) film on AA2024 were investigated under application of pulsed current as a function of Na3PO4 concentration in 0.05 M Na2SiO3 solution by analyzing voltage–time behavior, in-situ observation of arc generation, observation of surface morphology and measurements of thickness and surface roughness. Arc generation voltage decreased with increasing Na3PO4 concentration. Color difference of PEO films between edge and inner part disappeared by addition of Na3PO4. It was also observed that size of nodules on PEO film decreased with increasing Na3PO4 concentration. Thickness of PEO films formed on AA2024 increased with increasing Na3PO4 concentration. Whereas, surface roughness of PEO films decreased with increasing Na3PO4 concentration up to 0.05 M of Na3PO4 which is attributed to the deceased size of nodules on the PEO films. However, the surface roughness increased with increasing Na3PO4 concentration more than 0.07 M of Na3PO4 which seems to be due to the formation of non-uniform PEO films with smooth surface and large size pores formed by orange-colored big arcs. The experimental results suggest that added sodium phosphate less than 0.2 M in an alkaline silicate solution can contribute to the formation of relatively thick and uniform thickness of PEO films under arc generation voltage lower than 300 V.
참고문헌 (20)
- 문성모, "금속의 양극산화처리 기술", 한국표면공학회지, 51(1), pp.1~11 (2018), 한국표면공학회[DOI]
- A. L. Yerokhin, "Plasma electrolysis for surface engineering", Surface and Coatings Technology., 122, pp.73~ (1999)
- E. Matykina, "Recent advances in energy efficient PEO processing of aluminium alloys", Trans. Nonferrous Met. Soc. China, 27, pp.1439~1454 (2017)
- F. C. Walsh, "Plasma electrolytic oxidation (PEO) for production of anodised coatings on lightweight metal (Al, Mg, Ti) alloys", Transactions of the IMF, 87(3), pp.122~135 (2009)
- T. W. Clyne, "A review of recent work on discharge characteristics during plasma electrolytic oxidation of various metals", International Materials Reviews, 64(3), pp.127~162 (2019)
- 문성모, "Lateral Growth of PEO Films on Al1050 Alloy in an Alkaline Electrolyte", 한국표면공학회지, 50(1), pp.10~16 (2017), 한국표면공학회[DOI]
- S. Moon, "Anodic oxidation of Mg-Sn alloys in alkaline solutions", Corrosion Science, 65, pp.494~501 (2012)
- 권두영, "인산 및 규산 이온이 포함된 수용액에서 AZ31 마그네슘 합금의 플라즈마전해산화 피막의 구조에 미치는 수산화나트륨 농도의 영향", 한국표면공학회지, 49(1), pp.46~53 (2016), 한국표면공학회[DOI]
- 문성모, "PEO Film Formation Behavior of Al1050 Alloy Under Direct Current in an Alkaline Electrolyte", 한국표면공학회지, 50(1), pp.17~23 (2017), 한국표면공학회[DOI]
- S. Moon, "Generation mechanism of microdischarges during plasma electrolytic oxidation of Al in aqueous solutions", Corrosion Science, 51, pp.1506~1512 (2009)
- 문성모, "AZ31 마그네슘 합금의 플라즈마전해산화 피막 형성에 미치는 수산화 이온 및 규산 이온의 영향", 한국표면공학회지, 47(4), pp.147~154 (2014), 한국표면공학회[DOI]
- W. Liu, "Microstructure, wear and corrosion performance of plasma electrolytic oxidation coatings formed on D16T Al alloy", Rare Met, 39, pp.1425~1439 (2020)
- J. Lee, "Characterization of ceramic oxide coatings prepared by plasma electrolytic oxidation using pulsed direct current with different duty ratio and frequency", Applied Surface Science, 516, pp.146049~ (2020)
- A. V. Kolomeichenko, "Elemental Composition and Microhardness of the Coatings Prepared on Faced Aluminum Alloys by Plasma Electrolytic Oxidation in a Silicate–Alkaline Electrolyte", Russian Metallurgy(Metally), 13, pp.1410~1413 (2019)
- H. XIE, "Wear and corrosion resistant coatings on surface of cast A356 aluminum alloy by plasma electrolytic oxidation in moderately concentrated aluminate electrolytes", Trans. Nonferrous Met. Soc. China, 27, pp.336~351 (2017)
- Ding, ZY, "Insights into structure and high-temperature oxidation behavior of plasma electrolytic oxidation ceramic coatings formed in NaAlO2–Na2CrO4 electrolyte", J Mater Sci, 53, pp.9978~9987 (2018)
- Fattah-alhosseini, A., "Effects of Disodium Phosphate Concentration (Na2HPO4·2H2O) on Microstructure and Corrosion Resistance of Plasma Electrolytic Oxidation (PEO) Coatings on 2024 Al Alloy", J. of Materi Eng and Perform, 27, pp.825~834 (2018)
- 문성모, "AZ31 Mg합금의 PEO피막 형성거동에 미치는 인산나트륨 농도의 영향", 한국표면공학회지, 52(5), pp.265~274 (2019), 한국표면공학회[DOI]
- G. Lv, "Characteristic of ceramic coatings on aluminum by plasma electrolytic oxidation in silicate and phosphate electrolyte", Appl. Surf. Sci, 253, pp.2947~2952 (2006)
- 송의석, "6061 알루미늄 합금의 플라즈마 전해산화 피막의 표면기공율 및 부식특성에 미치는 Na3PO4 농도 및 NaAlO2 봉공처리의 영향", 한국표면공학회지, 52(3), pp.117~122 (2019), 한국표면공학회[DOI]