Pyroelectricity of BaTiO3-doped PMNT ferroelectric system for pyroelectric sensor
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, an MPB PMNT system containing 0.05 to 0.10 wt.% BaTiO3 was synthesized using a traditional chemical method and its pyroelectricity was investigated. Pyroelectricity, dielectricity, and ferroelectricity of the synthesized BaTiO3-PMNT system were analyzed by heat treatment at 1240~1280 oC for 4 hours to evaluate its applicability as a pyroelectric sensor. Unlike the simple ABO3 ferroelectric, the BaTiO3-doped PMNT system exhibited phase transition characteristics over a wide temperature range typical of complex perovskite structures. Although no dramatic change could be confirmed depending on the amount of BaTiO3 added, stable pyroelectricity was maintained near room temperature and over a wide temperature range. When the amount of BaTiO3 added increased from 0.05BaTiO3-PMNT to 0.10BaTiO3-PMNT, the electric field slightly increased from 5.00x103 kV/m to 6.75x103 kV/m, and the maximum value of remanent polarization slightly increased from
Abstract
In this study, an MPB PMNT system containing 0.05 to 0.10 wt.% BaTiO3 was synthesized using a traditional chemical method and its pyroelectricity was investigated. Pyroelectricity, dielectricity, and ferroelectricity of the synthesized BaTiO3-PMNT system were analyzed by heat treatment at 1240~1280 oC for 4 hours to evaluate its applicability as a pyroelectric sensor. Unlike the simple ABO3 ferroelectric, the BaTiO3-doped PMNT system exhibited phase transition characteristics over a wide temperature range typical of complex perovskite structures. Although no dramatic change could be confirmed depending on the amount of BaTiO3 added, stable pyroelectricity was maintained near room temperature and over a wide temperature range. When the amount of BaTiO3 added increased from 0.05BaTiO3-PMNT to 0.10BaTiO3-PMNT, the electric field slightly increased from 5.00x103 kV/m to 6.75x103 kV/m, and the maximum value of remanent polarization slightly increased from
참고문헌 (10)
- S. W. Choi, "Morphotropic phase boundary in Pb(Mg1", 3Nb2, Materials Letters, pp.1989, 8[DOI]
- A. Rittidech, "Investigation of phase formation and transition of(1-x)PMN-xPT in morphotropic phase boundary", Ferroelectrics, 355, pp.77~83 (2007)
- L. E. Cross, "Relaxor ferroelectrics : An overviews", Ferroelectrics, 151, pp.151~154 (1994)
- S. E. Park, "Ultrahigh strain and piezoelectric behavior in relaxor based ferroelectric single crystals", Journal of Applied Physics, 82, pp.1804~1811 (1997)
- X. Xia, "Critical state to achieve a giant electric field-induced strain with a low hysteresis in relaxor piezoelectric ceramics", Journal of Materiomics, 7, pp.1143~1152 (2021)
- J. Wang, "High piezoelectricity and low strain hysteresis in PMN–PTbased piezoelectric ceramics", Journal of advanced ceramics, 12, pp.792~802 (2023)
- D. Viehland, "Freezing of the polarization fluctuations in lead magnesium niobate relaxors", Journal of Applied Physics, 68, pp.2916~2921 (1990)
- A. J. Joseph, "New quaternary BNTBT-PMN-PT ceramic : ferro-", piezo-, Journal of Materials Science : Materials in Electronics, pp.2019, 30[DOI]
- Bobrek, "Temperature dependent electrical and electrocaloric properties of textured 0. 72PMN-0. 28PT ceramics", Integrated Ferroelectrics, 223, pp.214~227
- -textured Pb(Mg1, "3Nb2", 3)O3- PbTiO3 ceramics, 2012, pp.100, 192905~