전기 아연도금용 유색 크로메이트에 대한 건조 온도의 영향
The Effects of Drying Temperature on Chromate Treatment for Electroplated Zinc
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this study, the effect of drying temperature on characteristics of the trivalent chromate film on electroplated zinc was investigated. An zinc-electroplated iron specimen with a thickness of 5 μm was used for chromate treatment. Chromate treatment was conducted in a solution diluted 10 times from a mixture of Cr(NO3)3∙9H20 360 g/L, Co(NO3)2∙6H2O 60 g/L, Na2SO4 60 g/L, NH4F∙HF 25 g/L, and NaOH 20 g/L. The zinc electroplated specimen was treated using the chromate solution with pH 2.0 at 25 ℃ for 60 s. Subsequently, chromate-treated samples were dried in an electric furnace for 2h with temperature varied from 25 to 125 ℃. The corrosion rate increased with the increase in the drying temperature, and the surface morphology of the chromate-treated film was observed using FE-SEM. When the drying temperature changed, the color of the chromate film changed from green to yellow, and the thickness of the film changed from 362 to 241 nm, respectively. Additionally, corrosion resistance was evaluated via a salt spray test.
Abstract
In this study, the effect of drying temperature on characteristics of the trivalent chromate film on electroplated zinc was investigated. An zinc-electroplated iron specimen with a thickness of 5 μm was used for chromate treatment. Chromate treatment was conducted in a solution diluted 10 times from a mixture of Cr(NO3)3∙9H20 360 g/L, Co(NO3)2∙6H2O 60 g/L, Na2SO4 60 g/L, NH4F∙HF 25 g/L, and NaOH 20 g/L. The zinc electroplated specimen was treated using the chromate solution with pH 2.0 at 25 ℃ for 60 s. Subsequently, chromate-treated samples were dried in an electric furnace for 2h with temperature varied from 25 to 125 ℃. The corrosion rate increased with the increase in the drying temperature, and the surface morphology of the chromate-treated film was observed using FE-SEM. When the drying temperature changed, the color of the chromate film changed from green to yellow, and the thickness of the film changed from 362 to 241 nm, respectively. Additionally, corrosion resistance was evaluated via a salt spray test.
참고문헌 (16)
- C. T. Lee, "Ecological chromium plating by trivalent chromium", Journal of Industrial and Engineering Chemistry, 12, pp.831~840 (2001)
- 김수원, "아연도금용 친환경 3가 크로메이트 표면처리기술", 공업화학, 17(5), pp.433~442 (2006), 한국공업화학회
- 남기우, "크롬 프리 친환경 유", 무기 하이브리드 코팅액에 의한 냉연강판의 내식특성, 2013, pp.27(2), 33~38[DOI]
- V. Dikinis, "Characteristics of zinc corrosion and formation of conversion films on the zinc surface in acidic solutions of Cr(III)compounds", Transactions of the Institute of Metal Finishing, 82, pp.98~104 (2004)
- Z. L. Long, "Characterization of black chromate conversion coating on the electrodposited Zinc-iron alloy", Applied Surface Science, 218, pp.123~136 (2003)
- 이호종, "용융아연 도금욕에서 망간 산화물의 표면석출 거동", 한국표면공학회지, 48(1), pp.27~32 (2015), 한국표면공학회[DOI]
- "KS D 9502, Neutral, acetic acid and copper-accelerated acetic acid salt spray", Korean Standards & Certification, ~ (2020)
- KITECH, "Trivalent chromate solution for Zn electrodeposition composition, KR20100106031A", Korean Industrial Property Office, ~ (2009)
- 변종민, "g2Zn11 및 MgZn2 단일상의 부식거동", 대한금속·재료학회지, 51(6), pp.413~419 (2013), 대한금속·재료학회[DOI]
- S. H. Bae, "Effect of reaction product of epichlorohydrin and imidazole on the electrodeposition behavior of Zn-Ni alloy from alkaline zincate solution", ISIJ International, 61, pp.2256~2263 (2021)
- S. H. Bae, "Effect of solution temperature on electrodeposition behavior of Zn-Ni alloy from alkaline zincate solution", The Iron and Steel Institute of Japan, 108, pp.120~130 (2022)
- B. K. Son, "Zn-Ni alloy plating with trivalent chromate: effects of NaF additive concentration and treatment time on film color, thickness, and electrochemical properties", Coatings, 12, pp.1160~ (2022)
- D. E. Walker, "Enhanced molybdate conversion coatings", Ph. D, pp.2012
- D. G. Kim, "Chromate plating characteristics random-loaded of workpiece", Doctor, pp.2017
- Y. S. Kim, "Influences of chromate coating conditions on the surface appearance and corrosion resistance of aluminium alloys for can-stock", The Corrosion Science Society of Korea, 25, pp.180~191 (1996)
- L. F. G. Williams, "The effect of chromate Content on the corrosion of chromated zinc electroplate on steel", Surface Technology, 7, pp.113~127 (1978)