카본 나노튜브 및 알루미나 첨가제가 윤활 및 마모특성에 미치는 영향에 대한 연구
Study on Influence of Carbon Nanotubes and Alumina Additives to Lubrication and Wear Characteristics
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this work, carbon nanotube and nano-size alumina particle are exploited as additive for lubrication experiment. We used pin-on-disk type tribometer to investigate the tribological characteristics of lubricants with respect to additives and rotational speed. We conducted more than 15 trials of tribotests for two hours for each specimen to obtain stable and accurate frictional force and to create measurable wear track on the substrate. We conducted tests at the boundary/mixed lubrication regime to evaluate the influence of additives on the tribological characteristics. We found that the friction coefficient decreased as the rotational speed increased and as additives were added. In particular, the reduction of friction by adding additives was more significant at low rotational speed than at high rotational speed. We speculate that the additives helped to separate and protect the two contacting surfaces at low speed, while the influence of additives was not significant at high speed since sufficiently thick lubricant film was formed. The wear of the substrate was also reduced by adding additives to the lubricant. However, in contrast to friction, the amount of wear at high rotational speed was less when alumina particles were added to the lubricant than the amount of wear at low speed. We speculate that the increased wear at low rotational speed is as a result of the intermittent abrasive wear caused by alumina particles with uneven shape, while the reduced wear at high speed is as a result of sufficient film thickness which prevented the abrasive wear.
Abstract
In this work, carbon nanotube and nano-size alumina particle are exploited as additive for lubrication experiment. We used pin-on-disk type tribometer to investigate the tribological characteristics of lubricants with respect to additives and rotational speed. We conducted more than 15 trials of tribotests for two hours for each specimen to obtain stable and accurate frictional force and to create measurable wear track on the substrate. We conducted tests at the boundary/mixed lubrication regime to evaluate the influence of additives on the tribological characteristics. We found that the friction coefficient decreased as the rotational speed increased and as additives were added. In particular, the reduction of friction by adding additives was more significant at low rotational speed than at high rotational speed. We speculate that the additives helped to separate and protect the two contacting surfaces at low speed, while the influence of additives was not significant at high speed since sufficiently thick lubricant film was formed. The wear of the substrate was also reduced by adding additives to the lubricant. However, in contrast to friction, the amount of wear at high rotational speed was less when alumina particles were added to the lubricant than the amount of wear at low speed. We speculate that the increased wear at low rotational speed is as a result of the intermittent abrasive wear caused by alumina particles with uneven shape, while the reduced wear at high speed is as a result of sufficient film thickness which prevented the abrasive wear.
참고문헌 (23)
- 김현준, "Nano-scale Friction : A Review", International Journal of Precision Engineering and Manufacturing, 10(2), pp.141~151 (2009), 한국정밀공학회
- 한지희, "서브 마이크로 구조를 가진 실리콘 표면의 마찰 특성 연구", 한국윤활학회지, 33(3), pp.92~97 (2017), 한국윤활학회[DOI]
- Holmberg, K., "Coatings tribology :A concept, critical aspects and future directions", Thin Solid Films, 253, pp.173~178 (1994)
- Oh, D. -S., "Friction and deformation behaviors of ~60-μm stainless steel micro-balls for application in small precision devices", Tribol. Lett., 59(3), pp.1~10 (2015)
- Chouquet, C., "Effect of DLC surface texturing on friction and wear during lubricated sliding", Mater. Chem. Phys., 123, pp.367~371 (2010)
- Basnyat, P., "Surface texturing for adaptive solid lubrication", Surf. Coat. Technol, 203, pp.73~79 (2008)
- 김현준, "Nano-Lubrication: A Review", International Journal of Precision Engineering and Manufacturing, 17(6), pp.829~841 (2016), 한국정밀공학회
- Binu, K. G., "A variable viscosity approach for the evaluation of load carrying capacity of oil lubricated journal bearing with TiO2 Nanoparticles as Lubricant Additives", Procedia Mater. Sci., 6, pp.1051~1067 (2014)
- Tarasov, S., "Study of friction reduction by nanocopper additives to motor oil", Wear, 252, pp.63~69 (2002)
- Dong, J. X., "A study of the anti-wear and friction-reducing properties of the lubricant additive, nanometer zinc borate", Tribol. Int, 31, pp.219~223 (1998)
- Lee, K., "Understanding the role of nanoparticles in nano-oil lubrication", Tribol. Lett, 35, pp.127~131 (2009)
- Yao, Y., "Tribological property of onion-like fullerenes as lubricant additive", Mater. Lett, 62, pp.2524~2527 (2008)
- Kimura, Y., "Boron nitride as a lubricant additive", Wear, 232, pp.199~206 (1999)
- Guan, L., "Engine lubricating oil classification by SAE grade and source based on dielectric spectroscopy data", Anal. Chim. Acta., 628, pp.117~120 (2008)
- Cho, D. -H., "Evaluation of hexagonal boron nitride nanosheets as a lubricant additive in water", Wear, 302, pp.981~986 (2013)
- Eswaraiah, V., "Graphene-based engine oil nanofluids for tribological applications", ACS Appl. Mater. Interfaces, 3, pp.4221~4227 (2011)
- Lin, J., "Modification of Graphene Platelets and their Tribological Properties as a Lubricant Additive", Tribol. Lett., 41, pp.209~215 (2011)
- Chen, M., "The comparisons of sliding speed and normal load effect on friction coefficients of self-mated Si3N4 and SiC under water lubrication", Tribol. Int., 35, pp.129~135 (2002)
- Phillips, B. S., "Ionic liquid lubrication effects on ceramics in a water environment", Tribol. Lett., 17, pp.533~541 (2004)
- Chen, M., "Friction and wear of self-mated SiC and Si3N4 sliding in water", Wear, 250, pp.246~255 (2001)
- Kalin, M., "The Stribeck curve and lubrication design for non-fully wetted surfaces", Wear, 267, pp.1232~1240 (2009)
- Luo, T., "Tribological properties of Al2O3 nanoparticles as lubricating oil additives", Ceram. Int., 40, pp.7143~7149 (2014)
- Cornelio, J. A. C., "Tribological properties of carbon nanotubes as lubricant additive in oil and water for a wheel-rail system", J. Mater. Res. Technol., 5, pp.68~76 (2016)