그라파이트 나노윤활유의 열화 후 윤활 특성 비교 연구
Comparative Study to the Tribological Characteristics of Graphite Nano Lubricants after Thermal Degradation
2
조회
0
다운로드
8
인용
0
참고문헌
키워드
초록
Many researchers have tried to improve the tribological characteristics of lubricant by adding various nano particles in the base lubricant. But the reliability evaluation of the lubricants are rarely performed in its real operation condition. In this study, the physical property and the tribological haracteristics of the graphite nano lubricant were evaluated and compared with raw lubricant after thermal degrading. In order to evaluate the tirbological characteristics, the disk-on-disk tribotester was adopted to measure the friction coefficient of the graphite nano lubricants. Also the temperature variations of friction surfaces were measured by the thermocouple installed on the fixed plate in the test chamber of the tribotester. The kinematic viscosity was measured using a capillary viscometer on the temperatures of 40, 60 and 80oC. The results showed that the graphite nano lubricant had lower friction coefficient and less wear on the friction surfaces than raw lubricant. After thermally degrading, the friction coefficients of graphite nano lubricant increased, but the friction coefficients after thermal degradation were still maintained lower than those of raw lubricant.
Abstract
Many researchers have tried to improve the tribological characteristics of lubricant by adding various nano particles in the base lubricant. But the reliability evaluation of the lubricants are rarely performed in its real operation condition. In this study, the physical property and the tribological haracteristics of the graphite nano lubricant were evaluated and compared with raw lubricant after thermal degrading. In order to evaluate the tirbological characteristics, the disk-on-disk tribotester was adopted to measure the friction coefficient of the graphite nano lubricants. Also the temperature variations of friction surfaces were measured by the thermocouple installed on the fixed plate in the test chamber of the tribotester. The kinematic viscosity was measured using a capillary viscometer on the temperatures of 40, 60 and 80oC. The results showed that the graphite nano lubricant had lower friction coefficient and less wear on the friction surfaces than raw lubricant. After thermally degrading, the friction coefficients of graphite nano lubricant increased, but the friction coefficients after thermal degradation were still maintained lower than those of raw lubricant.
참고문헌 (14)
- Hsu,S.M, "Nano-lubrication:Concept and Design", Tribology International, 37, pp.537~545 (2004)
- Xue,Q., "Friction and Wear Properties of a Surface-modified TiO2 Nanoparticle as an Additive in Liquid Paraffin", Wear, 213, pp.29~32 (1997)
- Liu, G., "Investigation of the Mending Effect and Mechanism of Copper Nano-particles on a Tribologically Stressed Surface", Tribology Letters, 17(4), pp.961~966 (2004)
- Tao,X., "The Ball-bearing Effect of Diamond Nano Particles as an Oil Additivie", Journal of Physics, D26, pp.2932~2937 (1996)
- Chinas-Castillo, F, "Mechanism of Action of Colloidal Solid Dispersions", Transactions of the ASME, 125, pp.552~557 (2003)
- Qiu, S., "Tribological Properties of CeF3 Nanoparticles as Additives in Lubrication Oils", Wear, 230, pp.35~38 (1999)
- Rapoport, L., "Mechanism of Friction of Fullerene", Industrial Lubrication and Tribology, 54(4), pp.171~176 (2002)
- 안효석, "첨가제에 함유된 미세한 구리합금 입자의 마찰 및 마모 특성", 한국윤활학회지, 12(2), pp.32~40 (1996)
- 김중수, "엔진 오일 열화와 피스톤 온도가 카몬 디포짓 형성에 미치는 영향 Part II-디젤 엔진의 디포짓 형성 특성", 한국 윤활학회지, 14(2), pp.108~113 (1998)
- Lee, S, "Application of the Duplex TiN Coatings to Improve the Tribological Properties of Electro Hydrostatic Actuator Pump Parts", Surface & Coatings Technology, 193, pp.266~271 (2005)
- Lin, J., "The Tribological Performance of 6061 Aluminum Alloy", graphite Composite Materials in Oil Lubrications with EP Additives, 1996, pp.198, 58~70
- Lee, J., "Enhancing of Lubrication Properties of Nano-oil by Controlling the Amount of Fullerene Nanoparticle Additives", Tribology Letters, 28, pp.203~208 (2007)
- Luengo, G., "Generalized Effects in Confined Fluids:New Friction Map for Boundary Lubrication", Wear, 200, pp.328~335 (1996)
- 조용주, "마멸공학", 부산대학교 고장분석 및 신뢰성 연구센터, 153~153 (2003)