용매에 따른 MWNT의 분산특성과 제조된 PU/MWNT 필름의 전기적ㆍ물리적 특성 분석
Analysis of Electrical and Physical Property of the PU/MWNT Film and Dispersion Characteristics of MWNT According to the Solvent
1
조회
0
다운로드
4
인용
0
참고문헌
키워드
초록
This paper surveys the physical properties of the MWNT dispersion solution dispersed with the three types of solvents and of the polyurethane composite film for improvement of mechanical properties and electrical characteristics of PU/MWNT composite film. For this purpose, the MWNT dispersed solution was mixed with three types of solvent such as IPA, MEK and Toluene and then mixed with polyurethane (100part) with variation of loading content (0, 10, 20, 30, 40, 50 part) of MWNT dispersed solution in the ultrasonic wave dispersion apparatus. And eighteen PU/MWNT composite films were prepared as specimens. The various physical properties of these PU/MWNT films were measured and discussed with the loading content of three types of MWNT dispersed solutions. The highest absorbancy among the three types of dispersed solutions was shown in the IPA/MWNT solution. But the absorbancy of PU/MWNT films was not same as the solution. The low electrical surface and volume resistivity of PU/MWNT film were shown at the condition of 20 and 10 parts loading of IPA/MWNT dispersed solution,respectively. The low triboelectricity of PU/MWNT film was shown at the condition of above 30part loading of IPA/MWNT dispersed solution. The breaking strength and strain of PU/MWNT film prepared with IPA/MWNT dispersed solution were decreased with increasing loading content of IPA/MWNT from 10 to 40 parts. The maximum breaking strength and breaking strain according to the dispersion solution were shown on the IPA/MWNT dispersed solution. The uniform dispersion of PU/MWNT film according to the loading content of MWNT solution was shown by surface image analysis on the films dispersed with IPA.
Abstract
This paper surveys the physical properties of the MWNT dispersion solution dispersed with the three types of solvents and of the polyurethane composite film for improvement of mechanical properties and electrical characteristics of PU/MWNT composite film. For this purpose, the MWNT dispersed solution was mixed with three types of solvent such as IPA, MEK and Toluene and then mixed with polyurethane (100part) with variation of loading content (0, 10, 20, 30, 40, 50 part) of MWNT dispersed solution in the ultrasonic wave dispersion apparatus. And eighteen PU/MWNT composite films were prepared as specimens. The various physical properties of these PU/MWNT films were measured and discussed with the loading content of three types of MWNT dispersed solutions. The highest absorbancy among the three types of dispersed solutions was shown in the IPA/MWNT solution. But the absorbancy of PU/MWNT films was not same as the solution. The low electrical surface and volume resistivity of PU/MWNT film were shown at the condition of 20 and 10 parts loading of IPA/MWNT dispersed solution,respectively. The low triboelectricity of PU/MWNT film was shown at the condition of above 30part loading of IPA/MWNT dispersed solution. The breaking strength and strain of PU/MWNT film prepared with IPA/MWNT dispersed solution were decreased with increasing loading content of IPA/MWNT from 10 to 40 parts. The maximum breaking strength and breaking strain according to the dispersion solution were shown on the IPA/MWNT dispersed solution. The uniform dispersion of PU/MWNT film according to the loading content of MWNT solution was shown by surface image analysis on the films dispersed with IPA.
참고문헌 (18)
- G. W. Lee, "Dispersion of Carbon Nanotubes(CNTs) and CNT-based Transparent Conductive Films", KIC News, 10(4), pp.8~19 (2007)
- D. O. Kim, "Polymeric Carbon Nanotube Nanocomposites", Prospectives of Industrial Chemistry, 9(6), pp.3~13 (2006)
- J. Liu, "Fullerene Pipes", Science, 280, pp.1253~1256 (1998)
- 민병길, "PVA", 탄소나노튜브 복합수용액의 유변학적 특성과 전기방사특성에 관한 연구, 2006, pp.43(5), 251~256[DOI]
- 조재환, "전기응답 형상회복 특성을 갖는 탄소나노튜브-폴리우레탄 나노복합체", 한국섬유공학회지, 42(4), pp.270~276 (2005), 한국섬유공학회
- 원종열, "탄소나노튜브로 코팅된 전도성 섬유의 제조와 특성 분석", 한국섬유공학회지, 46(1), pp.1~7 (2009), 한국섬유공학회
- 조재환, "탄소나노튜브-폴리우레탄 나노복합체의 역학적, 열적 및 전기적 성질", 한국섬유공학회지, 41(2), pp.73~79 (2004), 한국섬유공학회
- 강민성, "전기방사에 의한 폴리아미드", 다중벽 탄소나노튜브 나노복합체섬유의 제조, 2008, pp.45(3), 159~165[DOI]
- H. Kitano, "Functionalization of Single-walled Carbon Nanotube by the Covalent Modification with Polymer Chains", J. Colloid Interface Sci., 306, pp.28~33 (2007)
- S. Musso, "Modification of MWNTs Obtained by Thermal- CVD", Diamond & Related Materials, 16, pp.1183~1187 (2007)
- T. Saito, "Chemical Treatment and Modification of Multiwalled Carbon Nanotubes", Physical B, 323, pp.280~283 (2002)
- A. Hirsch, "Functionalization of Single-Walled Carbon Nanotubes", Angew Chem. Int. Ed., 41, pp.1853~1859 (2002)
- M. Olek, "A Simple Route for the Attachment of Colloidal Nanocrystals to Noncovalently Modified Multiwalled Carbon Nanotubes", Colloids and Surfaces A: Physicochem Eng. Aspects，, 292, pp.83~85 (2007)
- I. Kumar, "Functionalization of Single-Walled Carbon Nanotubes with Azides Derived from Amino Acids Using Click Chemistry", Journal of Nanoscience and Nanotechnology, 8, pp.1~6 (2008)
- Y. Noguchi, "Single-walled Carbon Nanotubes", DNA Hybrids in Waterare Highly Stable, 2008, pp.455, 249~251
- 박경순, "분산성 향상을 위한 탄소나노튜브의 개질과 폴리우레탄과의 분산 특성", 한국염색가공학회지, 22(1), pp.43~50 (2010), 한국염색가공학회
- 김승진, "다중벽 탄소나노튜브와 폴리우레탄 복합화 필름의 물성특성", 한국염색가공학회지, 22(3), pp.246~256 (2010), 한국염색가공학회
- 박준형, "발포용 PU", MWNT 복합필름의 제조와 특성분석, 2010, pp.22(4), 362~372[DOI]