핵연료 피복관과 지지격자 사이에 발생하는 프레팅 마멸에 미치는 유동의 영향
The Effect of Water Flow on Fretting Wear of the Nuclear Fuel Cladding Tubes against the Supporting Grids
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
The flow induced vibration in the nuclear fuel assembly causes the fretting wear between the fuel cladding tubes and the supporting grids. The reduction in tube thickness due to the fretting wear could be related to the serious damage on nuclear fuel assembly. In this paper, the effect of the water flow on fretting wear of nuclear fuel cladding tube against supporting grid was investigated through the fretting wear tester with water spout equipment. The test results were compared with the data conducted in the stationary water. At stationary water environment the wear debris was trapped between fretting surfaces, and then the fretting wear occurred by three-body abrasion. However, in the case of water flow, the two-body abrasive wear was the dominant wear mechanism, because the wear debris was easily removed by water flow.
Abstract
The flow induced vibration in the nuclear fuel assembly causes the fretting wear between the fuel cladding tubes and the supporting grids. The reduction in tube thickness due to the fretting wear could be related to the serious damage on nuclear fuel assembly. In this paper, the effect of the water flow on fretting wear of nuclear fuel cladding tube against supporting grid was investigated through the fretting wear tester with water spout equipment. The test results were compared with the data conducted in the stationary water. At stationary water environment the wear debris was trapped between fretting surfaces, and then the fretting wear occurred by three-body abrasion. However, in the case of water flow, the two-body abrasive wear was the dominant wear mechanism, because the wear debris was easily removed by water flow.
참고문헌 (7)
- Abkra Iwabuchi, "The Role of Oxide Particles in the Fretting Wear of Mild Steel", Wear, 151, pp.301~311 (1991)
- M. Varengerg, "Different Aspects of the Role of Wear Debris in Fretting Wear", Wear, 252, pp.902~910 (2002)
- 한국원자력학회, "핵기계공학", pp.9~29 (1989)
- Dong-Goo Kim, "Experimental Investigation on Sliding and Fretting Wear of Steam Generator Tube Materials", Wear, 250, pp.673~680 (2001)
- Report NUREG, "P.E. MacDonald", 1~77, pp.CR-6365 (1996)
- S.H. Jeong, "Key Engineering Materials. Vol. 293-300", pp.1412~1417 (2005)
- Halliday,I.S., "The Fretting Corrosion of Mild Steel", Proc.Roy.Soc.Lond.,Ser.A, pp.411~425 (1956)