1-Step 연사공정 적용 나일론 연사물의 제조 및 특성 연구
Study on the Preparation and Properties of 1-Step Twisted Nylon Yarns
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Due to the change in lifestyle, new sensible materials for sportswear and outdoor are needed. This study is conducted in order to obtain the data for sensible materials through nylon twist process. 1-step nylon twisting machine was used to set the optimum twist process. DSC measurements of twisted nylon yarn showed crystallization temperatures around 170℃ and melting temperatures around 220℃. Nylon 40D/13F DTY and Nylon 50D/48F DTY showed optimal results at 160°C, 1,500 T/M(Turns per meter), and Nylon 70D/68F DTY at 160°C, 1,200 T/M(Turns per meter) after 1-step twist process. Also, Nylon 40D/13F DTY was confirmed to have inter-layer property deviation of ±5 percent.
Abstract
Due to the change in lifestyle, new sensible materials for sportswear and outdoor are needed. This study is conducted in order to obtain the data for sensible materials through nylon twist process. 1-step nylon twisting machine was used to set the optimum twist process. DSC measurements of twisted nylon yarn showed crystallization temperatures around 170℃ and melting temperatures around 220℃. Nylon 40D/13F DTY and Nylon 50D/48F DTY showed optimal results at 160°C, 1,500 T/M(Turns per meter), and Nylon 70D/68F DTY at 160°C, 1,200 T/M(Turns per meter) after 1-step twist process. Also, Nylon 40D/13F DTY was confirmed to have inter-layer property deviation of ±5 percent.
참고문헌 (11)
- 정명희, "황화염료를 이용한 고밀도 나일론 편성물의 염색성", 한국의상디자인학회지, 16(1), pp.117~123 (2014), 한국의상디자인학회
- D. H. Cho, "Development of NylonRelease TypeHigh-emotion SportsMaterial", The Korean Society of Clothing and Textiles, 2006(1), pp.208~ (2006)
- E. G. Lee, "The Study on the Physical Property of PET Filament in the 2-for-1 Twist Setting Process", Journal of the Korean Society of Dyers and Finishers, 12(2), pp.89~ (2000)
- D. J. Williams, "Polymer Science and Engineering", pp.36~38 (1971), Prentice Hall
- J. A. Brydson, "Plastics Materials", pp.23~24 (1995), Butterworths
- 정용식, "방사공법에 따른 나일론 섬유의 염색 특성성", 한국섬유공학회지, 44(2), pp.106~111 (2007), 한국섬유공학회
- W. H. Carothers, "Synthetic Fiber, U.S.Patent, 2,130, 948", ~ (1937)
- J. J. Kilian, "Process ofMelt Spinning and Stretching Filaments by Passing Them through Liquid Drag Bath, U.S.Patent, 3,002,804", ~ (1961)
- M. J., Piazza, "PolyesterYarn forDraw-Texturing Process, U.S.Patent, 3,772,872", ~ (1973)
- G. Heberlein, "Apparatus for Imparting False Twist to Yarn, U.S.Patent, 2,655,781", ~ (1953)
- J. M. Samon, "Study of the StructureDevelopment during the Melt Spinning ofNylon 6 Fiber byOn-LineWide-Angle Synchrotron X-ray Scattering Techniques", Journal of Polymer Science : Part B, Polymer Physics, 37, pp.1277~ (1999)