미끄럼 속도 변화에 따른 폴리우레탄 씰의 마모 특성
Effect of Sliding Speed on Wear Characteristics of Polyurethane Seal
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Hydraulic reciprocating seal has been widely used to prevent fluid leakage in hydraulic systems. Also, hydraulic reciprocating seal plays a significant role to provide lubricant film at contacting interface to minimize tribological problems due to sliding with counter material. To predict lifetime of hydraulic reciprocating seal, quantitative understanding of wear characteristics with respect to operating conditions such as normal force and sliding speed is needed. In this work, effect of sliding speed on wear of polyurethane (PU) hydraulic reciprocating seal were experimentally investigated using a pin-on-disk tribo-tester. The wear characteristics of PU specimens were quantitatively determined by comparing the confocal microscope data before and after test. It was found that the wear rate of PU specimens decreased from 4.9×10−11 mm3 to 1.1×10−11 mm3/Nm as sliding speed increased from 120 mm/s to 940 mm/s. Also, it was observed that the friction decreased slightly as the sliding speed increased. Improvement of lubrication state with increasing sliding speed was likely to be responsible for this enhanced friction and wear characteristics. This result also suggests that decrease in sliding distance between PU elastomer and counter materials at lower sliding speed is preferred. Furthermore, the quantitative assessment of wear characteristics of PU specimen may be useful in prediction of lifetime of PU hydraulic reciprocating seal if the allowed degree of wear for failure of the seal is provided.
Abstract
Hydraulic reciprocating seal has been widely used to prevent fluid leakage in hydraulic systems. Also, hydraulic reciprocating seal plays a significant role to provide lubricant film at contacting interface to minimize tribological problems due to sliding with counter material. To predict lifetime of hydraulic reciprocating seal, quantitative understanding of wear characteristics with respect to operating conditions such as normal force and sliding speed is needed. In this work, effect of sliding speed on wear of polyurethane (PU) hydraulic reciprocating seal were experimentally investigated using a pin-on-disk tribo-tester. The wear characteristics of PU specimens were quantitatively determined by comparing the confocal microscope data before and after test. It was found that the wear rate of PU specimens decreased from 4.9×10−11 mm3 to 1.1×10−11 mm3/Nm as sliding speed increased from 120 mm/s to 940 mm/s. Also, it was observed that the friction decreased slightly as the sliding speed increased. Improvement of lubrication state with increasing sliding speed was likely to be responsible for this enhanced friction and wear characteristics. This result also suggests that decrease in sliding distance between PU elastomer and counter materials at lower sliding speed is preferred. Furthermore, the quantitative assessment of wear characteristics of PU specimen may be useful in prediction of lifetime of PU hydraulic reciprocating seal if the allowed degree of wear for failure of the seal is provided.
참고문헌 (12)
- Nikas, G. K., "Eighty years of research on hydraulic reciprocating seals: Review of tribological studies and related topics since the 1930s", Proc. Inst. Mech. Eng. Part J-J. Eng. Tribol., 224, pp.1~23 (2010)
- Slater, C., "Compression set of thermoplastic polyurethane under different thermal-mechanical-moisture conditions", Polym. Degrad. Stab., 96, pp.2139~2144 (2011)[DOI]
- Qamar, S. Z., "Mechanical and structural behavior of a swelling elastomer under compressive loading", Mater. Des., 45, pp.487~496 (2013)[DOI]
- Orcutt, F. K., "An investigation of the operation and failure of mechanical face seals", J. Lubric. Tech., 91, pp.713~725 (1969)[DOI]
- Kim, H., "Effect of test parameters on degradation of polyurethane elastomer for accelerated life testing", Polym. Test., 40, pp.13~23 (2014)[DOI]
- Lee, S. H., "Accelerated wear test of FKM Elastomer for life prediction of seals", Polym. Test., 31, pp.993~1000 (2012)[DOI]
- Schmidt T., "A transient 2D-finite-element approach for the simulation of mixed lubrication effects of reciprocating hydraulic rod Seals", Tribol. Int., 43, pp.1775~1785 (2010)[DOI]
- Thatte, A., "Visco-elastohydrodynamic model of a hydraulic rod seal during transient operation", J. Tribol.-Trans. ASME, 132, pp.041501~ (2010)[DOI]
- Archard, J. F., "The wear of metals under ulubricated conditions", Proc. R Soc. A-Math. Phys. Eng. Sci., 236, pp.397~410 (1956)[DOI]
- Bae, J., "Accelerated wear testing of polyurethane hydraulic seal", Polym. Test., 63, pp.110~117 (2017)[DOI]
- 제영완, "부품 및 벤치 실험을 통한 폴리우레탄 유압왕복 실의 가속 실험", 한국트라이볼로지학회지, 30(5), pp.271~277 (2014), 한국트라이볼로지학회[DOI]
- Hill, D. J. T., "Laboratory wear testing of polyurethane elastomers", Wear, 208, pp.155~160 (1997)[DOI]