신축기능성 박지 Suede 직물의 역학적 성질 변화
The Mechanical Properties of Thin Suede Fabric with Stretch Function
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Although some degree of mechanical properties of suede fabrics mainly related to non-woven suede fabric has some researched, the thin suede fabric has rarely been researched. In this study, polyester(DTY 50/72) was used for warp, and after producing latent yarn and sea-island yarn for weft, two yarns were compounded to produce sea-island DTY yarn. By using the two produced yarns for warp and weft, we produced thin suede fabric with stretch function. For weft 2ply, weft density 85,90, 100(picks/in) were applied to weave fabric, and for weft 1ply, weft density 125, 135, 140(picks/in) were applied to produce weft face 5-end satin weave. The mechanical properties of the produced fabric were researched. The result are as followed. The weight loss ratio of the suede fabric produced for this experiment reached 15% on the conditions of temperature 90℃ and 20minutes, so that island parts were completely separated. The strength of weft 1ply applied suede fabric was about 7.5kg and that of 2ply suede fabric and about 3.5kg. But the strain of two samples ranged from about 40 to 43%. Although Hari was high when weft was denser. The values of Koshi and Kisimi were low. And shear stiffness was high when sea-island DTY yarn was used. The WC value was higher in the case of 2ply than in that of 1ply sea-island DTY yarn for weft, so that we may conclude that Fukurami was more affected in the 2ply case.
Abstract
Although some degree of mechanical properties of suede fabrics mainly related to non-woven suede fabric has some researched, the thin suede fabric has rarely been researched. In this study, polyester(DTY 50/72) was used for warp, and after producing latent yarn and sea-island yarn for weft, two yarns were compounded to produce sea-island DTY yarn. By using the two produced yarns for warp and weft, we produced thin suede fabric with stretch function. For weft 2ply, weft density 85,90, 100(picks/in) were applied to weave fabric, and for weft 1ply, weft density 125, 135, 140(picks/in) were applied to produce weft face 5-end satin weave. The mechanical properties of the produced fabric were researched. The result are as followed. The weight loss ratio of the suede fabric produced for this experiment reached 15% on the conditions of temperature 90℃ and 20minutes, so that island parts were completely separated. The strength of weft 1ply applied suede fabric was about 7.5kg and that of 2ply suede fabric and about 3.5kg. But the strain of two samples ranged from about 40 to 43%. Although Hari was high when weft was denser. The values of Koshi and Kisimi were low. And shear stiffness was high when sea-island DTY yarn was used. The WC value was higher in the case of 2ply than in that of 1ply sea-island DTY yarn for weft, so that we may conclude that Fukurami was more affected in the 2ply case.
참고문헌 (19)
- S. Yamauchi, "On the Present Condition and the Future Outlook of Automotive Interior Decoration Materials", Sen'i Gakkaishi, 59(8), pp.275~ (2003)
- Y. Tani, "Artifical Leater Having Grain", Japan Patent, 1998-062452, ~ (1998)
- M. Fujisawa, "Production of Nonwoven Fabric", Japan Patent, 1998- 062452, ~ (1998)
- Kolon Ltd., "A Sae-island Type Composite Fiber with Excellent Color Strength and its Suede like", Korean Patent, 100624145, ~ (2006)
- Kolon Ltd., "A Suede like Habric with Excellent Weight and Thickness", Korean Patent, 100681375, ~ (2007)
- D. W. Lim, "Manufacturing Method of the Artificial Leater that Aumospheric Corrosion Resistance is Excellent", Korean Patent, 1019930019401, ~ (1993)
- H. K. Lee, "Manufacturing Method of the Artificial Leater that Surface Effect is Excellent", Korean Patent, 1019940034786, ~ (1994)
- K. Nose, "The Microfibers Scene in Japan", Knitting International, 99(1179), pp.27~ (1992)
- "Various Microfibers for Clothing", pp.82~85 (1992), Japan Textile News
- J. E. Berkowitch, "In Tomorrow's Ideal and Profits: Polyester 50 Years of Achievement Textile Institute", pp.112~ (1993), Manchester
- M. Ymaguchi, "Development of "Z-10" Functional Fiber", Sen'i Gakkaishi, 58, pp.220~ (2002)
- O. Masakatsu, "Multi Functional Fiber “Z-10”", J. Text. Mach. Soc. of Japan, 52, pp.136~ (1999)
- Teijin Ltd., "Elastic Core-sheath Type Conjugate Yarn and Elastic Woven or Knitted Fabric", Japan Patent, 200200094558, ~ (2002)
- Hyosung Ltd., "Conjugate Spinning of Side by Side Nozzle", Korea Patent, 10-2002-0051300, ~ (2002)
- 박명수, "Super Bulky Yarn의 사가공 조건에 따른 물성변화", 한국의류산업학회지, 12(4), pp.500~507 (2010), 한국의류산업학회
- 심현주, "분할형 극세사를 이용한 습식인공피혁의 제조와 물리적 특성에 관한 연구", 한국섬유공학회지, 42(1), pp.48~53 (2005), 한국섬유공학회
- M. S. Park, "The Extraction of Co-PET from Non-Woven Fabrics of Nylon", Co-PET Sea-Island Type Composite Microfiber, 2001, pp.3, 466~
- Selivansky D, "Strain Phenomena of POY Revealed by Thermal Retraction and Other Techniques", J. Appl. Polym. Sci., 27, pp.2337~ (1982)
- 박명수, "복합가공사를 이용한 Wool-like 직물의 역학적성질", 한국의류산업학회지, 5(4), pp.408~412 (2003), 한국의류산업학회