In this research, split-type complex yarn of 20:80, 40:60, 50:50 nylon6/polyester composition ratio was used in order to impose unique sense on split-type complex woven. After treating both split-type complex yarn of each ratio and its produced woven in alkali solution, we got the following results by checking physical properties based on alkali proportion and treatment time. Under the condition of NaOH 20% in this experiment, it took approximately double time 20% loss of weight. The loss of weight became high when polyester proportion of N/P(nylon6/polyester) composition ratio was low, in the same fineness yarn. Even though polyester proportion was low, the loss of weight was low when the fineness was high. N/P division was well processed at about 25% loss of weight under the condition of NaOH 20%, treatment temperature 50℃, and treatment time 60 minutes. The research provides that the loss of weight should be processed around treatment time 24 hours in the case of NaOH concentration 15%, and treatment time 15 hours in the case of NaOH concentration 18%, respectively, in order to achieve N/P woven division ratio of about 70%-80% in industrial fields.
Abstract
In this research, split-type complex yarn of 20:80, 40:60, 50:50 nylon6/polyester composition ratio was used in order to impose unique sense on split-type complex woven. After treating both split-type complex yarn of each ratio and its produced woven in alkali solution, we got the following results by checking physical properties based on alkali proportion and treatment time. Under the condition of NaOH 20% in this experiment, it took approximately double time 20% loss of weight. The loss of weight became high when polyester proportion of N/P(nylon6/polyester) composition ratio was low, in the same fineness yarn. Even though polyester proportion was low, the loss of weight was low when the fineness was high. N/P division was well processed at about 25% loss of weight under the condition of NaOH 20%, treatment temperature 50℃, and treatment time 60 minutes. The research provides that the loss of weight should be processed around treatment time 24 hours in the case of NaOH concentration 15%, and treatment time 15 hours in the case of NaOH concentration 18%, respectively, in order to achieve N/P woven division ratio of about 70%-80% in industrial fields.
참고문헌 (11)
- V. L. Gibson, "An Analysis of the Bending and Shear Properties of Woven, Double-Knitted, and Warp-Knitted Outerwear Fabrics", Textile Res. J, 48(1), pp.14~ (1978)
- T. Hongu, "New Fibers" (1997), Woodhead
- E. J. Lee, "Texturing Studies on Split-type Microfine Polyester Filament Yarns", J. of Korean Fiber Society, 37(1), pp.25~ (2000)
- Y. Washino, "Functional Fibers" (1933), Today Research Center
- K. J. LEE, "Organic Solvent Absorption Characteristics of Split-Type Microfiber Fabrics", Fiber Polym, 5(4), pp.280~ (2004)
- S. J. Kim, "Effect of Chemical Split on Water Absorption of Split-type Polyester Microfiber Knit", Proceedings of the Korean Textile Conference, 33(1), pp.209~212 (2000)
- 서말용, "초음파를 적용한 PET 직물의 알칼리 가수분해에 관한 연구(Ⅰ)- 분해속도상수와 활성화 에너지 -", 한국염색가공학회지, 14(4), pp.18~26 (2002), 한국염색가공학회
- 홍성학, "열처리에 의한 폴리(트리메틸렌 테레프탈레이트) 섬유의 알칼리 가수분해 거동", 한국염색가공학회지, 15(3), pp.6~13 (2003), 한국염색가공학회
- 서말용, "해도형(海島型) PET 초극세섬유의 알칼리 가수분해에 관한 연구", 한국염색가공학회지, 25(4), pp.303~313 (2013), 한국염색가공학회
- 박명수, "ATY 사가공에 의한 Fluffy Spun-like Yarn의 물성 (1)", 한국염색가공학회지, 25(3), pp.223~231 (2013), 한국염색가공학회[DOI]
- M. S. Park, "A Study on the Crystal Structure of PET Films of by the Alkali Treatment", Textile Coloration and Finishing(J. of Korea Soc. Dyers and Finishers), 8(3), pp.206~ (1996)