Laser Peening: A Novel Tool to Reduce SCC Susceptibility and Prolong Fatigue Life of Metallic Components
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The effects of laser peening on metallic materials have been investigated with water-penetrable frequency-doubled Nd:YAG laser. Laser pulses of 200 mJ energy and 8 ns duration focused on samples underwater with 0.8 mm spot diameter. X-ray study showed that compressive residual stress was imparted on SKD61 from the surface to nearly 2 mm depth. Stress corrosion cracking (SCC) was prohibited for sensitized SUS304 even in a severely corrosive environment fatigue lives of SUS316L and SM490A welded samples were prolonged significantly in the high-cycle regime. Since 1999, laser peening has been applied to prevent SCC in operating nuclear power plants in Japan.
Abstract
The effects of laser peening on metallic materials have been investigated with water-penetrable frequency-doubled Nd:YAG laser. Laser pulses of 200 mJ energy and 8 ns duration focused on samples underwater with 0.8 mm spot diameter. X-ray study showed that compressive residual stress was imparted on SKD61 from the surface to nearly 2 mm depth. Stress corrosion cracking (SCC) was prohibited for sensitized SUS304 even in a severely corrosive environment fatigue lives of SUS316L and SM490A welded samples were prolonged significantly in the high-cycle regime. Since 1999, laser peening has been applied to prevent SCC in operating nuclear power plants in Japan.
참고문헌 (7)
- Sano Y, "Residual stress improvement in metal surface by underwater laser irradiation", Nucl.Instr.and Meth.B, 121, pp.432~436 (1997)
- Sano Y, "Residual stress improvement of weldment by laser peening", Weld.Int., 20, pp.598~601 (2006)
- Sano Y, "Retardation of crack initiation and growth in austenitic stainless steelsby laser peening without protective coating", Mater.Sci.Eng.A, 417, pp.334~340 (2006)
- Mukai N, "Preventive maintenance against stress corrosion cracking in nuclear power reactors by laser peening-Remote delivery of high-power pulsed laser-", Rev.LaserEng., 33, pp.444~451 (2005)
- Sano Y., "Underwater laser shock processing to introduce residual compressive stress on metals", Mater.Sci.Res.Int.,Special Technical Publication, 2, pp.453~458 (2001)
- Schmidt-Uhlig T, "New simplified coupling scheme for the delivery of 20MW Nd:YAG laser pulses by large core optical fibers", Appl.Phys.B, 72, pp.183~186 (2001)
- Sano Y., "Laser peening without coating to mitigate stress corrosion cracking and fatigue failure of welded components", Mater.Sci.Forum, 580, pp.519~522 (2008)