Aerosol deposition of thermoelectric p-type Bi0.5Sb1.5Te3 and n-type Bi2Te2.7Se0.3 thick films
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
A new aerosol deposition method was used to fabricate thick Bi-Te based thermoelectric films, such as p-type Bi0.5Sb1.5Te3 and n-type Bi2Te2.7Se0.3. The fabricated films exhibited dense morphologies without any large-scale porosity. Measured films thicknesses of Bi0.5Sb1.5Te3 and Bi2Te2.7Se0.3 were 276 µm and 557 µm, respectively. The thermoelectric properties of p-type Bi0.5Sb1.5Te3 and n-type Bi2Te2.7Se0.3 were measured to be 1.18 × 104 S/m and 0.7 × 104 S/m of electrical conductivities, 230.1 µV/K and -178 µV/K of Seebeck coefficients, 0.62 mW/mK2 and 0.21 mW/mK2 of power factors, respectively. It was demonstrated that the aerosol deposition is a promising thick film fabrication method for improving the thermoelectric efficiency of the thermoelectric materials
Abstract
A new aerosol deposition method was used to fabricate thick Bi-Te based thermoelectric films, such as p-type Bi0.5Sb1.5Te3 and n-type Bi2Te2.7Se0.3. The fabricated films exhibited dense morphologies without any large-scale porosity. Measured films thicknesses of Bi0.5Sb1.5Te3 and Bi2Te2.7Se0.3 were 276 µm and 557 µm, respectively. The thermoelectric properties of p-type Bi0.5Sb1.5Te3 and n-type Bi2Te2.7Se0.3 were measured to be 1.18 × 104 S/m and 0.7 × 104 S/m of electrical conductivities, 230.1 µV/K and -178 µV/K of Seebeck coefficients, 0.62 mW/mK2 and 0.21 mW/mK2 of power factors, respectively. It was demonstrated that the aerosol deposition is a promising thick film fabrication method for improving the thermoelectric efficiency of the thermoelectric materials
참고문헌 (15)
- D.M. Rowe, , Renew Energy, 16, pp.1251~1256 (1999)
- D.H. Kim, , Thin Solid Films, 510, pp.148~153 (2006)
- A.L. Bassi, , J. Appl. Phys, 105, pp.124307~ (2009)
- A. Bailini, , Applied Surface Science, 254, pp.1249~1254 (2007)
- L.W. da Silva, , J. Appl. Phys, 97, pp.114903~ (2005)
- F. Xiao, , Electrochim. Acta, 53, pp.8103~8117 (2008)
- X. Yan, , Nano Letter, 10, pp.3373~3378 (2010)
- D. Hanft, , J. Ceram. Sci. Tech, 06, pp.147~182 (2015)
- T. Varghese, , Scientific Reports, 6, pp.33135~ (2016)
- J. Exner, , Thin Solid Films, 573, pp.185~190 (2014)
- J. Akedo, , J. Therm. Spray Technol, 17, pp.181~198 (2008)
- J. Akedo, , Mater. Sci. Forum, 449-452, pp.43~48 (2004)
- J. Akedo, , J. Am. Ceram. Soc, 89, pp.1834~1839 (2006)
- D.Bourgault, , Thin Solid Films, 516, pp.8579~8583 (2008)
- H. Choi, , J. Mater. Chem. C, 5, pp.8559~8565 (2017)