Effect of Na2CO3 contents on synthesis of plate-like NaNbO3 particles for templated grain growth
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
x mol% (x = 0 ~ 20) Na2CO3 excess Bi2.5Na3.5Nb5O18 (BNN) particles were synthesized using molten salt as a flux. The secondary phases were observed at stoichiometric ratio of BNN precursors and their intensity decreased with increasing Na contents. The results of SEM images showed that all particles existed in a platelet shape and the particle increased in size with higher increasing Na contents. Plate-like NaNbO3 particles were developed using BNN precursor obtained by a topochemical microcrystal conversion. XRD analysis of NaNbO3 particles showed that a single perovskite phase and the intensity of (h00) peaks increased with increasing Na contents in BNN precursor. SEM images showed that the size of plate-like NaNbO3 was significantly changed by controlling Na contents in BNN precursors.
Abstract
x mol% (x = 0 ~ 20) Na2CO3 excess Bi2.5Na3.5Nb5O18 (BNN) particles were synthesized using molten salt as a flux. The secondary phases were observed at stoichiometric ratio of BNN precursors and their intensity decreased with increasing Na contents. The results of SEM images showed that all particles existed in a platelet shape and the particle increased in size with higher increasing Na contents. Plate-like NaNbO3 particles were developed using BNN precursor obtained by a topochemical microcrystal conversion. XRD analysis of NaNbO3 particles showed that a single perovskite phase and the intensity of (h00) peaks increased with increasing Na contents in BNN precursor. SEM images showed that the size of plate-like NaNbO3 was significantly changed by controlling Na contents in BNN precursors.
참고문헌 (15)
- R. E. Jaeger, , J. Am. Ceram. Soc, 45, pp.209~ (1962)
- G. H. Haertling, , J. Am. Ceram. Soc, 50, pp.329~ (1967)
- Y. Saito, , Nature, 432, pp.84~ (2004)
- H. Y. Park, , Appl. Phys. Lett, 89, pp.062906~ (2006)
- V. Bobnar, , Appl. Phys. Lett, 85, pp.994~ (2004)
- S. Zhang, , J. Appl. Phys, 100, pp.104108~ (2006)
- 윤중락, "The Piezoelectric Properties of (Na0.5K0.5)NbO3-K4CuNb8O23 Ceramics with Various K4CuNb8O23 Doping and Sintering Temperatures", Transactions on Electrical and Electronic Materials, 11(3), pp.126~129 (2010), 한국전기전자재료학회
- Y. Dai, , Appl. Phys. Lett, 90, pp.262903~ (2007)
- M. S. Kim, , Jpn. J. Appl. Phys, 48, pp.010204~ (2009)
- G. L. Messing, , Crit. Rev. Solid State Mater. Sci, 29, pp.45~ (2004)
- K.H. Brosnan, , J. Am. Ceram. Soc, 92, pp.S133~ (2009)
- Y. Yan, , J. Am. Ceram. Soc, 9(8), pp.2399~ (2007)
- Y. Chang, , Mater. Chem. Phys, 111, pp.195~ (2008)
- L. Zhao, , J. Cryst. Growth, 276, pp.446~ (2005)
- H. Takao, , J. Am. Ceram. Soc, 89, pp.1951~ (2006)