가스압 반응소결로 제조된 SiAlON 세라믹스의 상형성과 물리적 특성
Phase Formation and Physical Properties of SiAlON Ceramics Fabricated by Gas-Pressure Reactive Sintering
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
SiAlON-based ceramics are some of the most typical oxynitride ceramic materials, which can be used as cutting tools for heat-resistant super-alloys (HRSA). SiAlON can be fabricated by using gas-pressure reactive sintering from the raw materials, nitrides and oxides such as Si3N4, AlN, Al2O3, and Yb2O3. In this study, we fabricate Ybm/3Si12- (m+n)Alm+nOnN16-n (m=0.3, n=1.9, 2.3, 2.7) ceramics by using gas-pressure sintering at different sintering temperatures. Then, the densification behavior, phase formation, microstructure, and hardness of the sintered specimens are characterized. We obtain a fully densified specimen with β- SiAlON after gas-pressure sintering at 1820oC for 90 min. under 10 atm N2 pressure. These SiAlON ceramic materials exhibited hardness values of ~92.9 HRA. The potential of these SiAlON ceramics for cutting tool application is also discussed.
Abstract
SiAlON-based ceramics are some of the most typical oxynitride ceramic materials, which can be used as cutting tools for heat-resistant super-alloys (HRSA). SiAlON can be fabricated by using gas-pressure reactive sintering from the raw materials, nitrides and oxides such as Si3N4, AlN, Al2O3, and Yb2O3. In this study, we fabricate Ybm/3Si12- (m+n)Alm+nOnN16-n (m=0.3, n=1.9, 2.3, 2.7) ceramics by using gas-pressure sintering at different sintering temperatures. Then, the densification behavior, phase formation, microstructure, and hardness of the sintered specimens are characterized. We obtain a fully densified specimen with β- SiAlON after gas-pressure sintering at 1820oC for 90 min. under 10 atm N2 pressure. These SiAlON ceramic materials exhibited hardness values of ~92.9 HRA. The potential of these SiAlON ceramics for cutting tool application is also discussed.
참고문헌 (12)
- E. O. Ezugwu, , J. Mater. Process. Technol., 134, pp.233~ (2003)
- E. O. Ezugwu, "Key improvements in the machining of difficult-to-cut aerospace superalloys", Int. J. Mach. Tools Manuf, 45, pp.1353~1367 (2005)
- N. C. Acikbas, , J. Eur. Ceram. Soc., 32, pp.1321~ (2012)
- N. C. Acikbas, , Ceram. Inter., 39, pp.3249~ (2013)
- B. Bitterlich, , J. Eur. Ceram. Soc., 28, pp.989~ (2008)
- Y. M. Chiang, "Physcal Ceramics- Principles for Ceramic Science and Engineering", pp.69~ (1997), John Wiley & Sons
- V. Izhevskiy, , J. Eur. Ceram. Soc., 20, pp.2275~ (2000)
- A. Rosenflanz, , Curr. Opin. Solid State Mater. Sci., 4, pp.453~ (1999)
- H. Mandal, , J. Eur. Ceram. Soc., 19, pp.2349~ (1999)
- Mamoru Mitomo, "Materials Development in α-Sialon Ceramics", 한국세라믹학회지, 43(8), pp.451~457 (2006), 한국세라믹학회
- A. Rosenflanz, , J. Eur. Ceram. Soc., 19, pp.2325~ (1999)
- I. W. Chen, , Nature, 389, pp.701~ (1997)