M-type Sr-Hexaferrite에서 MnCO3 첨가에 따른 소결 거동
Sintering Behavior of M-type Sr-Hexaferrite by MnCO3 Addition
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The grain growth behavior of M-type Sr hexaferrite (SrM) grains is investigated with the addition of MnCO3. First, the SrM powder is synthesized by a conventional solid-state reaction. The powder compacts of SrM are sintered at 1250oC for 2 h with various amounts of MnCO3 (0, 0.5, 1.0, and 4.0 mol%). There is no secondary solid phase in any of the sintered samples. Relative density increases when MnCO3 is added to the SrM. Obvious abnormal grain growth does not appear in any of the SrM samples with MnCO3. The average grain size increases when 0.5 mol% MnCO3 is added to the SrM. However, as the amount of MnCO3 increase to over 0.5 mol%, the average grain size decreases. These observations allow us to conclude that the growth of SrM grains is governed by the two-dimensional nucleation grain growth mechanism, and the critical driving force for the growth of a grain decreases as the amount of MnCO3 increases.
Abstract
The grain growth behavior of M-type Sr hexaferrite (SrM) grains is investigated with the addition of MnCO3. First, the SrM powder is synthesized by a conventional solid-state reaction. The powder compacts of SrM are sintered at 1250oC for 2 h with various amounts of MnCO3 (0, 0.5, 1.0, and 4.0 mol%). There is no secondary solid phase in any of the sintered samples. Relative density increases when MnCO3 is added to the SrM. Obvious abnormal grain growth does not appear in any of the SrM samples with MnCO3. The average grain size increases when 0.5 mol% MnCO3 is added to the SrM. However, as the amount of MnCO3 increase to over 0.5 mol%, the average grain size decreases. These observations allow us to conclude that the growth of SrM grains is governed by the two-dimensional nucleation grain growth mechanism, and the critical driving force for the growth of a grain decreases as the amount of MnCO3 increases.
참고문헌 (28)
- R. C. Pullar, , Prog. Mater. Sci, 57, pp.1191~ (2012)
- K. J. Sixtus, , J. Appl. Phys, 27, pp.1051~ (1956)
- H. Nishio, , IEEE Trans. Magn, 44, pp.5281~ (2009)
- Y. -M. Kang, , Appl. Phys. Lett, 103, pp.122407~ (2013)
- J. Bai, , Mater. Sci. Eng. B, 68, pp.182~ (2000)
- Y. Ogata, , J. Jpn. Soc. Powder Powder Metall, 50, pp.636~ (2003)
- Y. -M. Kang, , J. Magn. Magn. Mater, 382, pp.10~ (2015)
- Y. -M. Kang, , Ceram. Int, 41, pp.12828~ (2015)
- Y. -M. Kang, , Ceram. Int, 41, pp.4354~ (2015)
- M. M. R. Boutz, , J. Eur. Ceram. Soc, 13, pp.89~ (1994)
- S.-J. L. Kang, (2005), Elsevier Butterworth-Heinemann
- S. M. Wang, , J. Am. Ceram. Soc, 91, pp.2617~ (2008)
- Y. I. Jung, , J. Mater. Res, 24, pp.2949~ (2009)
- P. W. Voorhees, , Metall. Trans. A, 15, pp.1081~ (1983)
- S. -J. L. Kang, , J. Am. Ceram. Soc, 92, pp.1464~ (2009)
- D. -Y. Yang, , J. Ceram. Soc. Jpn, 114, pp.970~ (2006)
- D. Y. Yoon, "The step growth hypothesis for abnormal grain growth" (2001)
- J. G. Fisher, , J. Eur. Ceram. Soc, 29, pp.2581~ (2009)
- B. K. Yoon, , Acta Mater, 57, pp.2128~ (2009)
- K. -S. Moon, , J. Eur. Ceram. Soc, 31, pp.1915~ (2011)
- Y. K. Cho, , J. Am. Ceram. Soc, 87, pp.443~ (2004)
- K. -S. Moon, , J. Appl. Phys, 120, pp.194102~ (2016)
- M. S. Kim, , J. Am. Ceram. Soc, 89, pp.1237~ (2006)
- B. K. Lee, , Acta Mater, 48, pp.1575~ (2000)
- Y. -I. Jung, , Acta Mater, 54, pp.2849~ (2006)
- K. -S. Moon, , J. Am. Ceram. Soc, 91, pp.3191~ (2008)
- 문경석, "Na0.5Bi0.5TiO3-BaTiO3 계에서 입자성장 및 고상단결정성장에 미치는 a2CO3 첨가 효과", 한국분말재료학회지, 25(2), pp.104~108 (2018), 한국분말재료학회[DOI]
- W. M. S. Silva, , J. Magn. Magn. Mater, 395, pp.263~ (2015)