폴리아크릴로니트릴 공중합체의 극세 섬유제조 및 그 물성
A Study of Fine Fiber Formation and Physical Properties of Polyacrylonitrile Copolymer
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The conditions of wet spinning were considered in order to prepare the fine denier of acrylic fiber. Polyacrylonitrile copolymer was synthesized by the copolymerization of acrylonitrile (AN) and methyl acrylate (MA) initiated by an aqueous sulfite-chlorate redox system. Acrylic fiber was manufactured through wet-spinning in a dimethyl formamide (DMF) system. The conditions of wet-spinning were investigated by i-value, spinning speed, diameter of spinneret,draw ratio, water content of spinning dope and morphology of protofiber. The physical properties of fibers were investigated by Instron. In this experiment, the minimum i-value decreased with the decreasing spinneret diameter, an increased spinning speed, and an increased coagulation bath (CBC) concentration. The maximum draw ratio increased with an increased CBC. The optimum CBC and water content of the spinning dope were 60%-65% and 3.5%, respectively. The tenacity at the breaking point increased with a decreased fineness of fiber. The elongation at breaking point was almost the same value as a function of the fineness of fiber.
Abstract
The conditions of wet spinning were considered in order to prepare the fine denier of acrylic fiber. Polyacrylonitrile copolymer was synthesized by the copolymerization of acrylonitrile (AN) and methyl acrylate (MA) initiated by an aqueous sulfite-chlorate redox system. Acrylic fiber was manufactured through wet-spinning in a dimethyl formamide (DMF) system. The conditions of wet-spinning were investigated by i-value, spinning speed, diameter of spinneret,draw ratio, water content of spinning dope and morphology of protofiber. The physical properties of fibers were investigated by Instron. In this experiment, the minimum i-value decreased with the decreasing spinneret diameter, an increased spinning speed, and an increased coagulation bath (CBC) concentration. The maximum draw ratio increased with an increased CBC. The optimum CBC and water content of the spinning dope were 60%-65% and 3.5%, respectively. The tenacity at the breaking point increased with a decreased fineness of fiber. The elongation at breaking point was almost the same value as a function of the fineness of fiber.
참고문헌 (11)
- Jeong, D., "Effect of Heat Treatment on Dyeing and Physical Properties of Nylon 6 Ultramicrofiber", Journal of the Korea Society of Dyers and Finishers, 14(6), pp.328~334 (2000)
- Kim, G., "New Synthetic Fiber", pp.318~319 (2001), Hyungseul
- 고준석, "직접방사형 PET 극세사 제품의 염색성 및 견뢰도 특성", 한국염색가공학회지, 17(5), pp.13~19 (2005), 한국염색가공학회
- 이혜정, "해도형 초극세 나일론 섬유의 알칼리 용출 및 염색성", 한국염색가공학회지, 22(4), pp.325~331 (2010), 한국염색가공학회
- Lee, K. S., "Dyeing Properties of Nylon 66 Nano Fiber with High Molecular Mass Acid Dyes", Fibers and Polymers, 6(1), pp.35~41 (2005)
- Lee, S., "Ripening Time and Fiber Formation of Chitosan Spinning Dope", Journal of Applied Polymer Science, 90, pp.2870~2877 (2003)
- Lee, S., "A Study on the Characterization and Properties of Acrylonitrile-Methylacrylate Copolymer Containning Vinylpyrrolidone and Polyvinylpyrrolidone", 박사, pp.1998
- Oh, J., "Dyeing Properties and Aftertreatment of UMF Nylon 6 Nonwoven Fabric", Journal of the Korea Society of Dyers and Finishers, 12(6), pp.344~352 (2000)
- Paul, D. R., "Spin Orientation during Acrylic Fiber Formation by Wet Spinning", Journal of Applied Polymer Science, 13(5), pp.817~825 (1969)
- Paul, D. R., "A Study of Spinnability in the Wet Spinning of Acrylic Fibers", Journal of Applied Polymer Science, 12(10), pp.2273~2298 (1968)
- "Various Microfibers for Clothing", Japan Textile News, 83~81 (1992)