Micro-porous ceramics using directionally solidified MgAl2O4/MgO eutectic crystals
3
조회
0
다운로드
0
인용
0
참고문헌
초록
Abstract
Novel process was tried to obtain micro-porous ceramic body containing continuous pore channel. MgAl2O4/MgO eutectic fibers and rods have been grown successfully by the micro-pulling-down method, and the microstructures and optical characterizations of grown crystals were performed. MgAl2O4/MgO eutectic fibers of 0.3~1 mm in diameter and about 500 mm in length, and the rods having 5 mm in diameter with approximately 60 mm in length have been grown with the 6~120 mm/hr of growth speed. The eutectic fibers showed homogeneous microstructure in which MgO fiber aligned to the growth direction in the MgAl2O4 (spinel) matrix. The grown crystals looked semitransparency under naked eyes. Optical and orientational characterizations were performed. The second phase of MgO (periclase) was easily removed by selective etching with hydrochloric acid, and then porous bodies were obtained.
참고문헌 (12)
- "Oriented eutectic micro-structures in the system Al2O3", ZrO2, 1970, ~
- "The eutectic and liquidus in the Al2O3", ZrO2system, 1981, ~
- "A ductile ceramic eutecticcomposite with high strength at 1", pp.873~389 (1997)
- "High-temperature strength and stability of aunidirectionally solidified Al2O3", YAG eutectic compos-ite, 1998, ~
- "Growth of Al2O3", Y3Al5O12 eutectic fiberby micro-pulling-down method and its high-tempera-ture strength and thermal stability, 1999, ~
- "Metastable alumina struc-tures in melt-extracted alumina-25 wt% zirconia andalumina-42 wt% zirconia ceramics" (1991)
- "Microstructure of Al2O3", ZrO2eutectic fibers grown by the micro-pulling-down method, 2001, ~
- "Microstructure of Y2O3 doped Al2O3", ZrO2 eutectic fibers by the micro-pulling-down method, 2001, ~
- "The effect of the microstruc-ture on mechanical properties of directionaly solidifiedAl2O3", ZrO2, 2000, ~
- "Growth of Al2O3", YAG[DOI]
- "Eutecticsolidification of MgO-MgAl2O4" (1973)
- "Mechani-cal properties of the directionally solidified MgO-MgAl2O4eutectic" (1976)