ZrB2 and YAG are widely applied because of some excellent properties, but ZrB2 is easily oxidized in high-temperature air. To make ZrB2 ceramics have better oxidation resistance, high-density YAG-ZrB2 ceramics were prepared. The oxidation behavior of YAG-ZrB2 ceramics is investigated at different temperatures. The results indicate that the enhanced weight change differs according to the temperature range, slightly in the temperature 900-1000oC, sharply from 1100-1300 and smoothly above 1300oC. The weight change rate of YAG-ZrB2 ceramics is increased by prolonging the oxidation time, but the weight change rate of YAG-ZrB2 ceramics is gradually reduced. The oxidation layer is porous as compared to the YAG-ZrB2 ceramics layer.
Abstract
ZrB2 and YAG are widely applied because of some excellent properties, but ZrB2 is easily oxidized in high-temperature air. To make ZrB2 ceramics have better oxidation resistance, high-density YAG-ZrB2 ceramics were prepared. The oxidation behavior of YAG-ZrB2 ceramics is investigated at different temperatures. The results indicate that the enhanced weight change differs according to the temperature range, slightly in the temperature 900-1000oC, sharply from 1100-1300 and smoothly above 1300oC. The weight change rate of YAG-ZrB2 ceramics is increased by prolonging the oxidation time, but the weight change rate of YAG-ZrB2 ceramics is gradually reduced. The oxidation layer is porous as compared to the YAG-ZrB2 ceramics layer.
참고문헌 (25)
- J.G. Song, , J. Disper. Sci. Tech., 28, pp.1072~1076 (2007)
- I.B. Bankovskaya, , Glass Phys. Chem., 31, pp.433~438 (2005)
- J.G. Song, , Mater. Manuf. Process, 23, pp.475~478 (2007)
- D. Sciti, , J. Am. Ceram. Soc., 89, pp.2320~2322 (2006)
- J.G. Song, , J. Reinf. Plast. Comp., 26, pp.139~145 (2007)
- A.L. Chamberlain, , J. Am. Ceram. Soc., 89, pp.450~456 (2006)
- J.G. Song, , Mater. Manuf. Process, 23, pp.98~101 (2008)
- A. Bellosi, , Int. J. Appl. Ceram. Tech., 3, pp.32~40 (2006)
- J.G. Song, , Surf. Rev. Lett., 16, pp.281~286 (2009)
- A. Fernandez, , J. Mater. Sci, 38, pp.2331~2335 (2003)
- M.B. Kakade, , J. Mater. Sci. Lett., 21, pp.927~929 (2002)
- F. Ivanauskas, , J. Math. Chem., 37, pp.365~372 (2005)
- X. Li, , J Alloy. Comp., 421, pp.298~302 (2006)
- M. Ono, , Appl. Phys. A., 74, pp.73~75 (2002)
- R.M. Laine, , Adv. Mater., 17, pp.830~833 (2005)
- S.J. Wang, , Mater. Sci. Eng. B., 127, pp.203~206 (2006)
- J.G. Song, , Surf. Rev. Lett., 14, pp.117~122 (2007)
- W.G. Fahrenholtz, , J. Am. Ceram. Soc., 88, pp.3509~3512 (2006)
- A. Rezaie, , J. Am. Ceram. Soc, 89, pp.3240~3245 (2006)
- E.J. Opila, , Ceram. Eng. Sci. Process, 22, pp.221~228 (2001)
- W.G. Fahrenholtz, , J. Am. Ceram. Soc., 90, pp.143~148 (2007)
- A. Rezaie, , J. Am. Ceram. Soc., 27, pp.2495~2501 (2007)
- R.L. Gao, , Ceram. Int., 31, pp.15~19 (2005)
- D. Sciti, , Scripta Mater., 53, pp.1297~1302 (2005)
- C.M. Chen, , Comp. Sci. Tech., 61, pp.971~975 (2001)