Heterostructured Nanophotocatalysts for Degradation of Organophosphate Pesticides from Aqueous Streams
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The present paper focuses on the synthesis, characterization and application of nanophotocatalyst for degradation of quinalphos and monocrotophos. Novel heterostructured ZnO/TiO2 photocatalyst (Z9T) was prepared and characterized with X-ray diffraction (XRD), SEM and UV-vis diffuses reflectance spectroscopy. The average crystalline size of synthesized Z9T was found to be 21.48 nm. The pesticides were degraded in the presence of nanophotocatalysts i.e., TiO2, ZnO, TiO2/ZnO mixed in various proportions and heterostructured nanophotocatalyst synthesized by Sol-Gel method. The batch experiments were performed by adding photocatalyst to 100 ml of pesticide solution and suspension was subjected to irradiation under UV light. In case of mixed catalyst, the maximum degradation of monocrotophos and quinalphos has been observed when ZnO and TiO2 were in the ratio of 7:3 and 8:2 respectively. The degradation efficiency with synthesized heterostructured nanophotocatalyst (Z9T) was found to be comparable with TiO2.
Abstract
The present paper focuses on the synthesis, characterization and application of nanophotocatalyst for degradation of quinalphos and monocrotophos. Novel heterostructured ZnO/TiO2 photocatalyst (Z9T) was prepared and characterized with X-ray diffraction (XRD), SEM and UV-vis diffuses reflectance spectroscopy. The average crystalline size of synthesized Z9T was found to be 21.48 nm. The pesticides were degraded in the presence of nanophotocatalysts i.e., TiO2, ZnO, TiO2/ZnO mixed in various proportions and heterostructured nanophotocatalyst synthesized by Sol-Gel method. The batch experiments were performed by adding photocatalyst to 100 ml of pesticide solution and suspension was subjected to irradiation under UV light. In case of mixed catalyst, the maximum degradation of monocrotophos and quinalphos has been observed when ZnO and TiO2 were in the ratio of 7:3 and 8:2 respectively. The degradation efficiency with synthesized heterostructured nanophotocatalyst (Z9T) was found to be comparable with TiO2.
참고문헌 (31)
- Yu, H., , Phys. Chem, 12, pp.6625~ (2010)
- Hoffmann, M. R., , Chem. Rev. (Washington, D.C.), 95, pp.69~ (1995)
- Fujishima, A., "U.S. Patent US6939611", ~ (2005)
- Sud, D., , Crit. Rev. Env. Sci. Tech, 42, pp.2365~ (2012)
- Mor, G. K., , Sensor Lett, 1, pp.42~ (2003)
- Bessa, E., , J. Adv. Oxid. Technol, 4, pp.196~ (1999)
- Cardoso, J. C., , Appl. Catal., B, 99, pp.96~ (2010)
- Reddy, P. S., , Pesticides, 20, pp.52~ (1986)
- Jena, M., , Oryza, 27, pp.96~ (1990)
- Banerjee, S. K., , Pestology, 24, pp.14~ (2000)
- Xu, Y., , Environ. Sci, pp.574~ (2002)
- Zhang, L., , J. Inorg. Mater, 42, pp.1379~ (2006)
- Doong, R., , J. Photochem. Photobiol., A, 107, pp.239~ (1997)
- Kralj, M. B., , Water Res, 41, pp.4504~ (2007)
- Moctezuma, E., , J. Photochem. Photobiol., A, 186, pp.71~ (2006)
- Anandan, S., , J. Mol. Catal. A: Chem, pp.149~ (2007)
- Anandan, S., , Catal. Commun, 10, pp.1014~ (2009)
- Shifu, C., , Solar Energy, 79, pp.1~ (2005)
- Kansal, S. K., , J. Hazard. Mater, 141, pp.581~ (2007)
- Bansal, P., , Desalin. Water Treat, 12, pp.108~ (2009)
- Bansal, P., , Sep. Purif. Technol, 72, pp.357~ (2010)
- Bansal, P., , Indian J. Chem., Sect. A, 50, pp.991~ (2011)
- Kansal, S. K., , Chem. Eng. Commun, 194, pp.787~ (2007)
- Rahman, A., , Desalination, 181, pp.161~ (2005)
- Gonclaves, M. S. T., , Chemosphere, 39, pp.781~ (1999)
- Kaur, P., , J. Mol. Catal. A: Chem, 365, pp.32~ (2012)
- Daneshvar, N., , J. Photochem. Photobiol., A, 162, pp.317~ (2003)
- Zhu, X. L., , J. Mol. Catal. A: Chem, 229, pp.95~ (2005)
- Liu, W., , Desalination, 249, pp.1288~ (2009)
- Pirkannicmi, K., , Chemosphere, 48, pp.1047~ (2002)
- Kansal, S. K., , Indian Chem. Eng., B, 47, pp.111~ (2006)