Noticeable localized corrosion of solid boric acid on 304 stainless steel

키워드

참고문헌 (60)

1. D. Xu, "Salt deposition problems in supercritical water oxidation", Chem. Eng. J, 279, pp.1010~1022 (2015)
2. M. Zhu, "Top of the REAC tube corrosion induced by under deposit corrosion of ammonium chloride and erosion corrosion", Eng. Fail. Anal, 57, pp.483~489 (2015)
3. W. Doniger, "Corrosion of 316L & 316H stainless steel in molten LiF-NaF-KF(FLiNaK)", J. Nucl. Mater, 579, pp.154383~ (2023)
4. Q. Xiong, "The study of under deposit corrosion of carbon steel in the flowback water during shale gas production", Appl. Surf. Sci, 523, pp.146534~ (2020)
5. M. H. Sliem, "Monitoring of under deposit corrosion for the oil and gas industry : a review", J. Pet. Sci. Eng, 204, pp.108752~ (2021)
6. G. H. Meier, "Invited review paper in commemoration of over 50 years of oxidation of metals : current aspects of deposit-induced corrosion", Oxid. Metals, 98, pp.1~41 (2022)
7. G. Hinds, "Novel multi-electrode test method for evaluating inhibition of under deposit Corrosion—Part 1 : sweet Conditions", Corrosion, 66, pp.046001~046001 (2010)
8. D. Han, "Mechanism of electrochemical corrosion of carbon steel under deoxygenated water drop and sand deposit", Electrochim. Acta, 114, pp.403~408 (2013)
9. M. Jeannin, "Role of a clay sediment deposit on the corrosion of carbon steel in 0. 5molL-1 NaCl solutions", Corrosion Sci, 52, pp.2026~2034 (2010)
10. M. Jeannin, "Role of a clay sediment deposit on the passivity of carbon steel in 0. 1moldm-3 NaHCO3 solutions", Electrochim. Acta, 56, pp.1466~1475 (2011)
11. S. Enestam, "Are NaCl and KCl equally corrosive on superheater materials of steam boilers?", Fuel, 104, pp.294~306 (2013)
12. N. Israelsson, "Cyclic corrosion and chlorination of an FeCrAl Alloy in the presence of KCl", Oxid. Metals, 84, pp.269~290 (2015)
13. J. Lehmusto, "Comparison of potassium chloride and potassium carbonate with respect to their tendency to cause high temperature corrosion of stainless 304L steel", Fuel Process. Technol, 105, pp.98~105 (2013)
14. K. V. Akpanyung, "An overview of ammonium chloride(NH4Cl)corrosion in the refining unit", J. Phys. Conf. Ser, 1378, pp.022089~ (2019)
15. S. Karlsson, "A laboratory study of the in situ sulfation of alkali chloride rich deposits : corrosion perspective", Energy Fuels, 30, pp.7256~7267 (2016)
16. S. Cassineri, "Deposition of corrosion products under pressurised water nuclear reactor conditions : the effect of flow velocity and dissolved hydrogen", Corrosion Sci, 159, pp.108113~ (2019)
17. Z. Y. Chen, "Effect of carbon dioxide on sodium chloride-induced atmospheric corrosion of copper", J. Electrochem. Soc, 152, pp.B502~ (2005)
18. H. Zheng, "Ultralong room-temperature phosphorescence from boric acid", Angew. Chem, 133, pp.9586~9592 (2021)
19. V. Vitola, "The role of boric acid in optical information storage properties in Eu doped BaSi2O5", J. Lumin, 243, pp.118682~ (2022)
20. U. Cabus, "Boric acid as a promising agent in the treatment of ovarian cancer: molecular mechanisms", Gene, pp.145799~ (2021)
21. Z. Zhang, "Selectively producing acetic acid via boric acid-catalyzed fast pyrolysis of woody biomass", Catalysts, 11 (2021)
22. K. Mehboob, "Analysis of activated colloidal crud in advanced and modular reactor under pump coastdown with kinetic corrosion", Nucl. Eng. Technol, 54, pp.4571~4584 (2022)
23. J. Gaillardet, "Evaporation and sublimation of boric acid : application for boron purification from organic rich solutions", Geostand. Geoanal. Res, 25, pp.67~75 (2001)
24. R. Balasubramanian, "Investigation of the vaporization of boric acid by transpiration thermogravimetry and Knudsen effusion mass spectrometry", J. Phys. Chem. B, 112, pp.13873~13884 (2008)
25. A. Bruggeman, "Method for Separating Boric Acid", EP, ~ (1995)
26. T. A. Lang, "Aging Manag. Compon. Anal", pp.169~176 (2003), ASMEDC
27. R. Vaghetto, "Experimental observations of boric acid precipitation scenarios", Nucl. Eng. Des, 312, pp.422~428 (2017)
28. C. T, "PWSCC of austenitic stainless steels of heaters of pressurizers", Contrib. Mater. Investig. Improve Saf. Perform. LWRs-Fontevraud 6 SFEN Fr, ~ (2008)
29. Y. Xu, "Microstructural evolution and oxidation behaviour of CF8A austenitic stainless steel during corrosion fatigue in a simulated pressurised water reactor environment", Corrosion Sci, 163, pp.108286~ (2020)
30. Y. S. Lim, "Corrosion behavior of SA508 low alloy steels exposed to aerated boric acid solutions", Nucl. Eng. Technol, pp.S1738573319306230~ (2019)
31. C. Ma, "Effect of polishing process on corrosion behavior of 308L stainless steel in high temperature water", Appl. Surf. Sci, 442, pp.423~436 (2018)
32. M. H. Sliem, "Monitoring of under deposit corrosion for the oil and gas industry : a review", J. Petrol. Sci. Eng, 204, pp.108752~ (2021)
33. W. Wang, "Revealing of corrosion behavior of GH4169 under the alternate environment of intermediate temperature NaCl spraying and marine atmosphere", J. Mater. Res. Technol, 22, pp.2316~2327 (2023)
34. X. Li, "Non-negligible corrosion from vaporized boric acid on 304 stainless steel", J. Nucl. Mater, 574, pp.154188~ (2023)
35. M. Le Calvar, "Corrosion issues in pressurized water reactor (PWR)systems", Nucl. Corros. Sci. Eng, pp.473~547 (2012)
36. X. Wang, "Long-term under-deposit pitting corrosion of carbon steel pipes", Ocean Eng, 133, pp.231~243 (2017)
37. M. A. Diaz-Mateus, "Effect of deposit chemistry on microbial community structure and activity: implications for underdeposit microbial corrosion", Front. Microbiol, 14 (2023)
38. S. Aghili, "The kinetics and mechanism of B2O3formation from the chemically-synthesized HBO2 under non-isothermal conditions", React. Kinet. Mech. Catal (2021)
39. J. L. Parsons, "Vibrational spectra of vitreous B2O3. xH2O", J. Am. Ceram. Soc, 43, pp.326~330 (1960)
40. J. Xu, "The evolution of electrochemical behaviour and oxide film properties of 304 stainless steel in high temperature aqueous environment", Electrochim. Acta, 71, pp.219~226 (2012)
41. X. Li, "Heat-induced morphology-dependent corrosion of solid boric acid on carbon steel", J. Mater. Sci. Technol, 29, pp.4547~4557 (2024)
42. T. Jonsson, "Oxidation after breakdown of the chromium-rich scale on stainless steels at high temperature : internal oxidation", Oxid. Metals, 85, pp.509~536 (2016)
43. H. Liu, "Revealing the temperature effects on the corrosion behaviour of 2205 duplex stainless steel from passivation to activation in a CO2-containing geothermal environment", Corrosion Sci, 187, pp.109495~ (2021)
44. Y. Chen, "OnePot preparation of autonomously self-healable elastomeric hydrogel from boric acid and random copolymer bearing hydroxyl groups", ACS Macro Lett, 6, pp.1129~1133 (2017)
45. X. Li, "Efficient removal of boron acid by Nmethyl-d-glucamine functionalized silica–polyallylamine composites and its adsorption mechanism", J. Colloid Interface Sci, 361, pp.232~237 (2011)
46. M. Zhao, "Adhesion effect and mechanism of siderophore-producing bacteria onto goethite and boron-doped goethite", J. Colloid Interface Sci, 51, pp.100680~ (2022)
47. J. Robertson, "The mechanism of high temperature aqueous corrosion of stainless steels", Corrosion Sci, 32, pp.443~465 (1991)
48. Q. Liu, "Corrosion behaviour of 316 stainless steel in NaCl-KCl-MgCl2 salt vapour at 700◦C", Corrosion Sci, 194, pp.109921~ (2022)
49. W. Kuang, "The mechanism of oxide film formation on Alloy 690 in oxygenated high temperature water", Corrosion Sci, 53, pp.3853~3860 (2011)
50. L. G. Ling, "Investigation of the oxides film on 304L base metal produced during welding process without inert gas shielding", Appl. Surf. Sci, 465, pp.780~786 (2019)
51. B. H. Tran, "Hot corrosion of borate melt and interface chemistry of borate-coated steel under tribological stimulation", Corrosion Sci, 140, pp.231~240 (2018)
52. T. Takei, "Effect of boron distribution on the intergranular corrosion resistance of UNS S32506 duplex stainless steels", J. Electrochem. Soc, 166, pp.C375~C381 (2019)
53. K. Kruska, "Nanoscale characterisation of grain boundary oxidation in cold-worked stainless steels", Corrosion Sci, 63, pp.225~233 (2012)
54. C. Schmidt, "Boron speciation in aqueous fluids at 22 to 600◦C and 0. 1 MPa to 2 GPa", Geochem. Cosmochim. Acta, 69, pp.275~281 (2005)
55. Z. Shen, "Fretting wear-induced sudden loss of corrosion resistance in a corrosion-resistant Ni-based alloy", Mater. Char, 201, pp.112955~ (2023)
56. H. Zhang, "Effect of HAc on the metastable pitting corrosion of 304 SS in NaCl solution", Materials, 15, pp.3618~ (2022)
57. A. Vesel, "High temperature oxidation of stainless steel AISI316L in air plasma", Appl. Surf. Sci, 255, pp.1759~1765 (2008)
58. J. Yuan, "Comparison between the oxidation of iron in oxygen and in steam at 650–750◦C", Corrosion Sci, 75, pp.309~317 (2013)
59. L. Guo, "Excellent corrosion resistance of 316stainless steel in purified NaCl-MgCl2 eutectic salt at high temperature", Corrosion Sci, 166, pp.108473~ (2020)
60. A. Rehman, "Hot corrosion behaviour of yttrium and aluminium modified wear resistance coating alloy in mixed sulphate at 900 ◦C", Corrosion Sci, 165, pp.108369~ (2020)

관련 논문AI추천