Effect of Additives on the Stress Corrosion Cracking Behavior of Alloy 600 in High Temperature Caustic Solutions
2
조회
0
다운로드
0
인용
0
참고문헌
초록
Abstract
The effect of inhibitors on the electrochemical behavior and the stress corrosion cracking resistance of Alloy 600(UNS N06600) was evaluated in 10% sodium hydroxide solution at 315℃. The specimens of a C-ring type for stress corrosion cracking test were polarized at 150 mV above the corrosion potential for 120 hours with and without inhibitors such as titanium oxide, titanium boride and cerium boride. The chemical compositions of the films formed on the crack tip in the C-ring specimens were analyzed using a scanning Auger electron spectroscopy. The cerium boride, the most effective, was observed to decrease the crack propagation rate more than a factor of three compared with that obtained in no inhibitor solution. It was found that the changes of the active-passive transition potentials and the film compositions were related to the resistance to stress corrosion cracking in high temperature caustic solution.
참고문헌 (11)
- "Steam Generator Progress Report", 14 (1999), EPRI
- "PWR Molar Ratio Control Application Guidelines" (1995), EPRI
- "Correlation of Secondary-Side IGA", SCC Degradation of Recirculating Steam Generator Tubing With the On-Line Addition of Boric Acid, 1992, ~
- "Mechanism and Effectiveness of Inhibitors for SCC in a Caustic Environment", pp.137~ (1995), NACE
- "Slow Strain Rate Testing to Evaluate Inhibitors for Stress Corrosion Cracking of Alloy 600 Proc. 6th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems- Water Reactors", pp.303~ (1993)
- "Model Boiler Testing to Evaluate Inhibitors for Caustic Induced Stress Corrosion Cracking of Alloy 600 Tubes", pp.177~ (1995), NACE
- "Secondary Degradation of Steam Generator Tubing: Which Inhibitors for Which Causes? A Review of Model Boiler Test Results", pp.100~ (1997), ANS
- "Stress Corrosion Crack Tip Microstructure in Nickel-Base Alloys", paper(154), pp.~94 (1994)
- "Use of Pourbaix Diagrams to Infer Local Pitting Conditions" (1986)
- "Inhibition of Intergranular Attack and Stress Corrosion Cracking With Boric Acid Proc. Third Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors", j.p.(pae), pp.511~ (1987)
- "Steam Generator Tube Failures", pp.105~ (1996), U.S. Nuclear Regulatory Commission