Effects of Melting Condition and Alloying Elements on Localized Corrosion Resistance of High Cr and N Bearing Stainless Steels

Abstract

In this study, the characteristics of the experimentally produced high N-high Cr bearing stainless steels are discussed as a part of applications of materials for FGD (Fuel Gas Desulfurization) system of thermal power plants or for power plants using seawater as coolant. Corrosion resistance of developed alloys is especially investigated in detail. Corrosion characteristics of vacuum melted cast are shown to be superior to that of air melted one. From the viewpoint of CPT, It is estimated that the differences of corrosion resistance are 21.8℃~24.6℃ at PRE 40 and 8℃~12.4℃ at PRE 50, and the gaps becomes bigger as the PRE values are lower. In the evaluation of corrosion resistance in alloy A2501, Z3101, and A3301 according to Cr concentration, alloy A3301 shows a deviation from the general tendency in chloride solutions. It has relatively high PRE value as 48.6, but it has relatively poor pitting resistance. It is, however, difficult to observe a specific phase except ferrite in microstructure analysis and neither detects special phase such as sigma phase.