Corrosion Behaviour of Some Alloys in Tropical Urban and Marine Atmospheres
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Results of corrosion testing for different grades of titanium, copper, zinc, alluminium alloys and steels after two years of outdoor exposure under humid tropical urban and marine conditions have been presented and discussed. Mass loss and corrosion product characteristics for the exposed specimens at Hanoi testing site with high humidity and Nhatrang marine stations (at 100 and 1,000 meters distances from sea) with different airborne salinities (35.9 and 90.0 mg/m2.d respectively) have been selected for investigation. From time dependence of the specimen mass loss and corrosion product characteristics, the strong influence of environmental parameters upon durability for the investigated metals and alloys has been demonstrated. Only titanium alloys show high resistance to the marine conditions. All the other specimens (copper, zinc, alluminium alloys and steels) have been underwent strong deterioration under influence of aerosol salinity. Results of corrosion products analysis have been also presented for characterization of environmental impact on the metal degradation processes.
Abstract
Results of corrosion testing for different grades of titanium, copper, zinc, alluminium alloys and steels after two years of outdoor exposure under humid tropical urban and marine conditions have been presented and discussed. Mass loss and corrosion product characteristics for the exposed specimens at Hanoi testing site with high humidity and Nhatrang marine stations (at 100 and 1,000 meters distances from sea) with different airborne salinities (35.9 and 90.0 mg/m2.d respectively) have been selected for investigation. From time dependence of the specimen mass loss and corrosion product characteristics, the strong influence of environmental parameters upon durability for the investigated metals and alloys has been demonstrated. Only titanium alloys show high resistance to the marine conditions. All the other specimens (copper, zinc, alluminium alloys and steels) have been underwent strong deterioration under influence of aerosol salinity. Results of corrosion products analysis have been also presented for characterization of environmental impact on the metal degradation processes.
참고문헌 (5)
- I. S. Cole, , the 11th APCCC, pp.555~ (1999)
- Nguyen viet Hue, , the 11th APCCC, pp.582~ (1999)
- Le Thi Hong Lien, "“Corrosion of zinc coatings in Vietnam atmospheric environments”", Ph. D., pp.2005
- Tran Thi Ngoc Lan, "“Environmental Characteristics and Materials Damage in Soth Vietnam”", Ph. D., pp.2004
- Nguyen Duc Hung, , the 16th ICC (2005)