A reaction and evaporation types of cerium based conversion coatings were developed for galvanized steel sheet. The corrosion loss Q(Cb/cm²) and protection efficiency P(%) were obtained using a polarization technique for cerium based conversion coatings on galvanized steel exposed to 0.5N NaCl for 7 days. The microstructure of coating layer was observed using SEM. An excellent corrosion reistnce of galvanized steel was obtained by two types of cerium basd conversion coating. Salt spray test was done to evaluate the corrosion resistance of three samples by visual inspection. The corrosion ranking of three samples-untreated and two treatedby electrochemical data was matched well with the results of salt spray test.
Abstract
A reaction and evaporation types of cerium based conversion coatings were developed for galvanized steel sheet. The corrosion loss Q(Cb/cm²) and protection efficiency P(%) were obtained using a polarization technique for cerium based conversion coatings on galvanized steel exposed to 0.5N NaCl for 7 days. The microstructure of coating layer was observed using SEM. An excellent corrosion reistnce of galvanized steel was obtained by two types of cerium basd conversion coating. Salt spray test was done to evaluate the corrosion resistance of three samples by visual inspection. The corrosion ranking of three samples-untreated and two treatedby electrochemical data was matched well with the results of salt spray test.
참고문헌 (28)
- Aeberli, Karl Edward, "Metallurgical plant and technology international", MPT 23(4), pp.8~ (2000)
- "Conversion coating, Alubook/<"[URL]
- H. J. Ashmead, , J. Appl. Nutrition, 24, pp.8~ (1972)
- M. S. Vukasovich, , Materials Perfor Performances, 25, pp.9~ (1986)
- N. Zaki, , Metal Finishing, 88, pp.99~ (1990)
- B. R. W. Hinton, , Metals Forum, 7, pp.211~ (1984)
- B. R. W. Hinton, , Mater. Forum, 9, pp.162~ (1986)
- You Wang, ""Corrosion protection of Aluminum alloys by surface modification using chromate free approaches"", Ph. D, pp.1994
- Z. Sun, ""Application of electrochemical methods incorrosion and battery research"", Ph.D, pp.2001
- B. R. W. Hinton, , Corros Sci, 29, pp.967~ (1989)
- "International Patent WO 88", 06639
- M. Geary, , Corr. Sci, 39, pp.1341~ (1997)
- G. D. Wilcox, , Corros. Sci, 28, pp.577~ (1988)
- G. D. Wilcox, , Brit. Corros. J, 22, pp.254~ (1987)
- A. C. Cross land, , Corrosion Sci, 40, pp.871~ (1998)
- F. Mansfeld, , J. Electrochem.Soc, 145, pp.2792~ (1998)
- F. M. Seon, , J. Less Common Metals, 148, pp.73~ (1989)
- S. Boehm, , Jr. Electrochem. Sci, 147, pp.3286~ (2000)
- A. J. Aldykiewicz, , J. Electrochem. Soc, 143, pp.147~ (1996)
- A. J. Davenport, , Corros. Sci, 32, pp.653~ (1991)
- B. R. W. Hinton, , Metals Forum, 7, pp.211~ (1984)
- B. R. W. Hinton, ""Effect of Cerous Chloride Concentration on Corrosion Rate", Australian patent, PCT", AU88, ~
- A. E. Hughes, , Surf. Inter. Anal, 23, pp.540~ (1995)
- F. Mansfeld, , Corrosion, 45, pp.615~ (1989)
- F. Mansfeld, , ASTM STP (1993)
- J. A. V. Butler, , Transactions of the Faraday Society, 19, pp.729~ (1924)
- T. Redey-Gruz, , Zeitschrift fur Physikund Chemie, 150A, pp.203~ (1930)
- V. Barranco, , Corros. Sci, 46, pp.2221~ (2004)