Aluminum is on active metal, but it is well known that its oxide film plays a role as protective barrier which is comparatively stable in air and neutral aqueous solution. Thus, aluminum alloys have been widely applied in architectural trim, cold & hot-water storage vessels and piping etc., furthermore, the aluminum alloy of AC8A have been widely used in mold casting material of engine piston because of its properties of temperature and wear resistance. In recent years, the oil price is getting higher and higher, thus the using of low quality oil has been significantly increased in engines of ship and vehicle. Therefore it is considered that evaluation of corrosion resistance as well as wear resistance of AC8A material is also important to improve its property and prolong its lifetime. In this study, the effect of solution and tempering heat treatment to corrosion and wear resistance is investigated with electrochemical method and measurement of hardness. The hardness decreased with solution heat treatment compared to mold casting condition, but its value increased with tempering heat treatment and exhibited the highest value of hardness with tempering heat treatment temperature at 190 ℃ for 24hrs. Furthermore, corrosion resistance increased with decreasing of the hardness, and decreased with increasing of the hardness reversely. As a result, it is suggested that the optimum heat treatment to improve both corrosion and wear resistance is tempering heat treatment temperature at 190 ℃ for 16hrs.
Abstract
Aluminum is on active metal, but it is well known that its oxide film plays a role as protective barrier which is comparatively stable in air and neutral aqueous solution. Thus, aluminum alloys have been widely applied in architectural trim, cold & hot-water storage vessels and piping etc., furthermore, the aluminum alloy of AC8A have been widely used in mold casting material of engine piston because of its properties of temperature and wear resistance. In recent years, the oil price is getting higher and higher, thus the using of low quality oil has been significantly increased in engines of ship and vehicle. Therefore it is considered that evaluation of corrosion resistance as well as wear resistance of AC8A material is also important to improve its property and prolong its lifetime. In this study, the effect of solution and tempering heat treatment to corrosion and wear resistance is investigated with electrochemical method and measurement of hardness. The hardness decreased with solution heat treatment compared to mold casting condition, but its value increased with tempering heat treatment and exhibited the highest value of hardness with tempering heat treatment temperature at 190 ℃ for 24hrs. Furthermore, corrosion resistance increased with decreasing of the hardness, and decreased with increasing of the hardness reversely. As a result, it is suggested that the optimum heat treatment to improve both corrosion and wear resistance is tempering heat treatment temperature at 190 ℃ for 16hrs.
참고문헌 (12)
- H. Y. Lee, "Metal Corrosion Engineering", pp.262~ (1991), Yeon Kyung Culture Co. Ltd
- M. Y. Doshi, "Nonferrous Metal Matewrial Engineering", pp.144~ (1975), KoRoNa Co. Ltd
- Mars. G. Fontana, "Corrosion Engineering", pp.236~ (1986), McGraw Hill Book company
- Deny A. Jones, "Principles and Prevention of CORROSION", pp.262~522 (1996), Prentice Hall International, Jnc
- A. Muhlend bruch, , Z. Metallkde, 31, pp.239~ (1989)
- H. Borchers, , Metall, 21, pp.1215~ (1967)
- Y. M. Bashi, , J. Met. Soc. of Japan, 36, pp.341~ (1972)
- Y. D. Kmura, , J. Lig. Met. Soc. of Japan, 22, pp.403~ (1972)
- S. N. Thuri, , J. Met. Soc. of Japan, 37, pp.110~ (1973)
- R. H. Brown, "The Resistance of Wrought High Strength aluminum alloys to Stress Corrosion Cracking", ASTM. STP, 518, pp.87~ (1972)
- R. E. Stoltz, , Metall. Trans, 3, pp.2433~ (1972)
- 신재현, "보수용접봉의 종류와 용접후 열처리가 용접금속부의 내식성에 미치는 영향에 관한 전기화학적 평가", CORROSION SCIENCE AND TECHNOLOGY, 9(6), pp.310~316 (2010), 한국부식방식학회