Study on Hygrothermal Degradation and Corrosion Protection of Epoxy Coatings Cured by Different Amine Based Curing Agents
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Epoxy coatings cured by different amine based curing agents have been prepared. Atomic force microscopy (AFM) has been used to monitor the surface topology changes of epoxy coatings before and after hygrothermal cyclic test. The glass transition temperature (Tg) and coefficient of thermal expansion (CTE) of the epoxy coating were measured by Thermo-mechanical Analysis (TMA). The Electrochemical impedance spectroscopy (EIS) with hygrothermal cyclic test has been introduced to evaluate the corrosion protection of the epoxy coatings. In conclusion, thermal properties of epoxy coatings were in good agreement with the results of corrosion protection of epoxy coated carbon steel obtained result by EIS with hygrothermal cyclic test. The relationship between thermal properties, surface roughness changes and corrosion protection of epoxy coatings are discussed in this study.
Abstract
Epoxy coatings cured by different amine based curing agents have been prepared. Atomic force microscopy (AFM) has been used to monitor the surface topology changes of epoxy coatings before and after hygrothermal cyclic test. The glass transition temperature (Tg) and coefficient of thermal expansion (CTE) of the epoxy coating were measured by Thermo-mechanical Analysis (TMA). The Electrochemical impedance spectroscopy (EIS) with hygrothermal cyclic test has been introduced to evaluate the corrosion protection of the epoxy coatings. In conclusion, thermal properties of epoxy coatings were in good agreement with the results of corrosion protection of epoxy coated carbon steel obtained result by EIS with hygrothermal cyclic test. The relationship between thermal properties, surface roughness changes and corrosion protection of epoxy coatings are discussed in this study.
참고문헌 (16)
- "ISO 7253, Paints and varnishes -- Determination of resistance to neutral salt spray", ~
- B.S. Skerry, , Corrosion, 49, pp.663~ (1993)
- S.L. Chong, , JPCL, 14, pp.20~ (1997)
- G.P. Bierwagen, , Prog. Org. Coat., 39, pp.67~ (2000)
- J. Li, , Corrosion, 54, pp.763~ (1998)
- Homma, K, , NACE Corrosion, 91, pp.9~ (1991)
- Homma, K, , ASTM STP 1137, ~ (1992)
- Davis, Guy H., , Mater. Perform., 39, pp.46~ (2000)
- Mansfeld, F, , Corrosion, 47, pp.958~ (1991)
- Tsai, C.H, , Corrosion, 49, pp.726~ (1993)
- J. Li, , Corrosion, 54, pp.763~ (1998)
- Gordon P. Bierwagen, , Prog. Org. Coat., 39, pp.67~ (2000)
- L. Valentinelli, , Prog. Org. Coat., 45, pp.405~ (2002)
- L. Fedrizzi, , Prog. Org. Coat., 48, pp.271~ (2003)
- S. Touzain, , Prog. Org. Coat., 52, pp.311~ (2005)
- L. Fedrizzi, "Evaluation of accelerated aging procedures of painted galvanised steels by EIS", Electrochim. Acta, 51, pp.1864~ (2006)