PWR 1차측 환경에서 Alloy 600응력부식균열 선단 부근에서의 산화 거동
Oxidation Behavior around the Stress Corrosion Crack Tips of Alloy 600 under PWR Primary Water Environment
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
Stress corrosion cracks in Alloy 600 compact tension specimens tested at 325 ℃ in a simulated primary water environment of pressurized water reactor were analyzed by analytical transmission electron microscopy and secondary ion mass spectroscopy (SIMS). From a fine-probe chemical analysis, oxygen was found on the grain boundary just ahead of the crack tip, and chromium oxides were precipitated on the crack tip and the grain boundary attacked by the oxygen diffusion, leaving a Cr/Fe depletion (or Ni enrichment) zone. The oxide layer inside the crack was revealed to consist of a double (inner and outer) layer. Chromium oxides existed in the inner layer, with NiO and (Ni,Cr) spinels in the outer layer. From the nano-SIMS analysis, oxygen was detected at the locations of intergranular chromium carbides ahead of the crack tip, which means that oxygen diffused into the grain boundary and oxidized the surfaces of the chromium carbides. The intergranular chromium carbide blunted the crack tip, thereby suppressing the crack propagation.
Abstract
Stress corrosion cracks in Alloy 600 compact tension specimens tested at 325 ℃ in a simulated primary water environment of pressurized water reactor were analyzed by analytical transmission electron microscopy and secondary ion mass spectroscopy (SIMS). From a fine-probe chemical analysis, oxygen was found on the grain boundary just ahead of the crack tip, and chromium oxides were precipitated on the crack tip and the grain boundary attacked by the oxygen diffusion, leaving a Cr/Fe depletion (or Ni enrichment) zone. The oxide layer inside the crack was revealed to consist of a double (inner and outer) layer. Chromium oxides existed in the inner layer, with NiO and (Ni,Cr) spinels in the outer layer. From the nano-SIMS analysis, oxygen was detected at the locations of intergranular chromium carbides ahead of the crack tip, which means that oxygen diffused into the grain boundary and oxidized the surfaces of the chromium carbides. The intergranular chromium carbide blunted the crack tip, thereby suppressing the crack propagation.
참고문헌 (24)
- W. Bamford, , Proceedings of the 11th Int'l Conf. on Environmental Degradation of Materials in Nuclear Power Systems, pp.1071~ (2003)
- W. Bamford, , Proceedings of the 12th Int'l Conf. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactor, pp.959~ (2005)
- W. Bamford, , Proceedings of the 13th Int'l Conf. on Environmental Degradation of Materials in Nuclear Power Systems (2007)
- H. Xu, , Proceedings of the 12th Int'l Conf. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactor, pp.833~ (2005)
- F. P. Ford, , Corrosion, 52, pp.375~ (1996)
- H. K. Birnbaum, , Mater. Sci. Eng., A, 176A, pp.191~ (1994)
- T. Magnin, , Proceedings of the 6th Int'l Conf. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactor, pp.669~ (1993)
- P. M. Scott, , Proceedings of the 9th Int'l Conf. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactor, pp.3~ (1999)
- L. E. Thomas, , Corrosion, 56, pp.572~ (2000)
- P. Laghoutaris, , ICG-EAC 2008 (2008)
- M. Sennour, , J. Nuc. Mater, 393, pp.254~ (2009)
- M. Olszta, , ICG-EAC 2011 (2011)
- M. A. Hicks, , Int. J. of Fracture, 20, pp.91~ (1982)
- G. A. White, , Proceedings of the 11th Int'l Conf. on Environmental Degradation of Materials in Nuclear Power Systems, pp.166~ (2003)
- Y. S. Lim, , Mater. Char, 60, pp.1496~ (2009)
- R. H. Bricknell, , Acta. Metall, 30, pp.257~ (1982)
- R. G. Iacocca, , Metall. Trans. A, 19A, pp.2305~ (1988)
- R. W. Staehle, , Proceedings of the 9th Int'l Conf. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactor, pp.69~ (1999)
- J. Panter, , J. Nuc. Mater, 348, pp.213~ (2006)
- J. Robertson, , Corros. Sci, 32, pp.443~ (1991)
- Optimization of Metallurgical Variables to Improve Corrosion Resistance of Inconel 600, "G. P. Airey", ~, pp.EPRI Report No. NP-3051 (1983)
- S. M. Bruemmer, , Scripta Metall, 20, pp.909~ (1986)
- Seong Sik Hwang, "SCC Mechanism of Ni Base alloys in Lead Contaminated Water", CORROSION SCIENCE AND TECHNOLOGY, 7(3), pp.189~193 (2008), 한국부식방식학회
- K. Fujii, , ICG-EAC 2011 (2011)