불소도포제에 의한 치면열구전색제의 마모저항성과 표면 변화에 관한 실험연구
Experimental Research on the Surface Changes and the Abrasion Resistance of Pit and Fissure Sealant by Fluoride
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
To test the effects of representative fluoride vanishes−1.23% APF gel and 5% NaF Fluoride Varnish−on the surface structure of pit and fissure sealant, this study classified samples of pit and fissure sealant into five groups: Group I deposited in distilled water for ten minutes, Group II treated with APF gel for one minute, Group III treated with APF gel for four minutes, Group IV treated with Fluoride Varnish for one minute, and Group V treated with Fluoride Varnish for four minutes. An abrasion test was carried out to measure changes in weight, along with observation of the surface structure by using an optical microscope, consequently drawing the following conclusions. 1. The results of the abrasion test using pit and fissure sealant, Concise, showed that Group III had the reduction in weight more increased than Group I and that Group V had less reduction in weight (p<0.05); the results of the abrasion test using Eco-S showed Group III had the reduction in weight more increased than Group I and that Group V had less reduction in weight (p<0.05). 2. The results of observation using an optical microscope showed that application of APF gel made the filler remarkable due to loss of substrate and that Group III treated with APF gel for four minutes had the toughest surface, followed by Group II treated with APF gel for one minute, Group I deposited in distilled water for ten minutes, Group IV treated with Fluoride Varnish for one minute, and Group V treated with Fluoride Varnish for four minutes.
Abstract
To test the effects of representative fluoride vanishes−1.23% APF gel and 5% NaF Fluoride Varnish−on the surface structure of pit and fissure sealant, this study classified samples of pit and fissure sealant into five groups: Group I deposited in distilled water for ten minutes, Group II treated with APF gel for one minute, Group III treated with APF gel for four minutes, Group IV treated with Fluoride Varnish for one minute, and Group V treated with Fluoride Varnish for four minutes. An abrasion test was carried out to measure changes in weight, along with observation of the surface structure by using an optical microscope, consequently drawing the following conclusions. 1. The results of the abrasion test using pit and fissure sealant, Concise, showed that Group III had the reduction in weight more increased than Group I and that Group V had less reduction in weight (p<0.05); the results of the abrasion test using Eco-S showed Group III had the reduction in weight more increased than Group I and that Group V had less reduction in weight (p<0.05). 2. The results of observation using an optical microscope showed that application of APF gel made the filler remarkable due to loss of substrate and that Group III treated with APF gel for four minutes had the toughest surface, followed by Group II treated with APF gel for one minute, Group I deposited in distilled water for ten minutes, Group IV treated with Fluoride Varnish for one minute, and Group V treated with Fluoride Varnish for four minutes.
참고문헌 (23)
- 이상호, "치면열구전색의 유지력", J Korean Pediatr Dent, 33(2), pp.336~347 (2006)
- Simomsen RJ, "Retention and effectiveness of dental sealants after 15 years", J Am Dent Assoc, 122, pp.34~42 (1991)
- Primosch RE, "Sealant use and placement techniques among pediatric dental", J Am Dent Assoc, 132, pp.1442~1451 (2001)
- 김희진, "불소도포 방법에 따른 법랑질 불소 결합 효과", 석사, pp.2009
- Bibby BG, "The effect of fluorine on mouth bacteria", J Dent Res, 19, pp.391~402 (1940)
- gaard, B, "Fluoride retention in sound and demineralized enamel in vivo after treatment with a fluoride varnish(Duraphat)", Scand J Dent Res, 92, pp.190~197 (1984)
- 임성수, "Fluoride varnish 도포가 초기 법랑질 우식 병소의 재석회화에 미치는 영향에 관한 연구", 대한소아치과학회지, 20(1), pp.131~134 (1993)
- Weintraub JA, "Fluoride of fluoride varnish efficacy in preventing early childhood caries", J Dent Res, 85(2), pp.172~176 (2006)
- 한윤범, "Acidulated phosphate fluoride에 의한 치면열구전색제의 미세 표면 변화", 석사, pp.2010
- 최유성, "수종의 인공레진 치아의 마모저항성과 경도에 관한 비교 연구", 석사, pp.2008
- 최원혁, "APF Gel이 심미 수복재료의 표면에 미치는 영향", 대한소아치과학회지, 33(2), pp.281~289 (2006), 대한소아치과학회
- Knuston JW, "The effect of topically applied sodium fluoride on dental caries experience", Publ Health Rep, 58, pp.1701~1715 (1943)
- Arends J, "Efefect of various fluoride on enamal structure and chemistry", Cariology today, pp.245~258 (1984)
- Ten Cate, J.M, "In vitro studies on effects of fluoride on deand remineralization", J Dent Res, 69, pp.614~619 (1990)
- Scholtanus JD, "Influence of fluoridating varnishes on dentine in vitro", Caries Res, 20(1), pp.65~70 (1986)
- Cueto El, "Sealant of pits and fissures with an adhesive resin: its use in caries prevention", J Am Dent Assoc, 75, pp.121~128 (1967)
- Gwinnett AJ, "Penetration of pit and fissure sealants into conditioned human enamel in vivo", Arch Oral Biol, 18, pp.435~439 (1973)
- Horowitz AM, "Effective oral health education and promotion programs to prevent dental caries", Int Dent J, 33, pp.171~181 (1983)
- Simonsen RJ, "Retention and effectiveness of a single application of white sealant after 10 years", J Am Dent Assoc, 115, pp.31~36 (1987)
- 장종화, "불소이온영동에 의한 법랑질 표면 불소농도의 주사전자현미경적 관찰", 치위생과학회지, 6(4), pp.303~307 (2006)
- Kula KS, "Effect of 1-and 4-minute treatments of topical fluorides on a composite resin", Pediatr Dent, 18, pp.24~28 (1996)
- Garcia-Godoy F, "Effect of APF Minute-Form on the surface roughness, hardness, and micromorphology of high-viscosity glass ionomers", J Dent Child, 70, pp.19~23 (2003)
- 윤명옥, "불소바니쉬가 법랑질 탈회에 미치는 영향", 석사, pp.2007